| for documentation of Perple_X thermodynamic data file structure and content refer to: | www.perplex.ethz.ch/perplex_thermodynamic_data_file.html | comments are indicated by the | character. | check for warnings at the end of the header section. | this file can only be read by Perple_X 6.7.8+ | the Holland and Powell data for aqueous species does not appear to be maintained | and has been moved to hpAQver.dat. Holland & Powell, JMG 2011 (TC-DS633, 23 Jun,2017) + additional data |<= data base title | WARNING WARNING WARNING WARNING WARNING WARNING WARNING WARNING WARNING!!! | WARNING WARNING WARNING WARNING WARNING WARNING WARNING WARNING WARNING!!! | WARNING WARNING WARNING WARNING WARNING WARNING WARNING WARNING WARNING!!! | Data for the following endmembers in this file has been eliminated by | commenting, to make the data accessible remove the comment characters: | nta - Na-talc | tap - talc-pyrophyllite | mic - microcline | tan - an unknown variant on the talc endmember | Additionally the "fact" (ferro-actinolite) endmember has been renamed | "ftr" to maintain consistency with ds5 data files. | data from other sources (HSC, SUPCRT, etc) has been added at the end of this | file. JADC, Oct 12, 2022. begin_standard_variables |<= name (<9 characters), reference value, tolerance P(bar) 1.00 0.1E-3 T(K) 298.15 0.1E-4 Y(CO2) 0.00 0.1E-6 mu(C1) 0.00 0.1E-2 mu(C2) 0.00 0.1E-2 end_standard_variables tolerance -.1E-2 |<= DTOL for unconstrained minimization, energy units HSC_conversion |<= tag enabling HSC to SUP apparent energy conversion, requires elemental entropies in the component list below begin_components | < 6 chars, molar weight (g), elemental entropy (R) Na2O 61.9790 205.1750 MgO 40.3040 135.2550 Al2O3 101.9610 364.4250 SiO2 60.0840 223.9600 K2O 94.1960 231.9350 CaO 56.0770 144.2050 TiO2 79.8660 235.8700 MnO 70.9370 134.7950 FeO 71.8440 129.8550 NiO 74.6930 132.3750 ZrO2 123.2200 244.3300 Cl2 70.9060 223.0800 O2 31.9990 205.1500 H2O 18.0150 233.2550 CO2 44.0100 210.8900 CuO 79.5450 135.7250 Cr2O3 151.9900 358.8110 S2 64.1300 64.1000 F2 37.9968 202.79 N2 28.013 191.610 end_components begin_special_components H2O CO2 end_special_components begin_makes | the make definitions segment of the thermodynamic | data file is preceded by the "begin_makes" keyword, | and terminated by the "end_makes" keyword. Within | this segment comments must be preceded by a "|" | character. | the make definitions define new thermodynamic entities | (e.g., fO2 buffers, endmembers etc) as a linear combination of | the "real" entities in the thermodynamic file. the definition | includes a "DQF" correction that is used to increment the | G of the linearly combined G's as a function of pressure and | temperature, i.e., the total G computed for a made entity is | the G of the right-hand-side of the make reaction + Gdqf. | the format assumes data on one line of less than 240 characters, | the expected format is | name = num_1 * name_1 + num_2 * name_2 ....+ num_int * name_int | dnum_1 dnum_2 dnum_3 | where i num_j is a number or fraction (i.e., two numbers separated | by a '/') and name_j are the names of the j existing entities. | and the dqf correction to the entity 'name' is | Gdqf(J/mol) = dnum_1 + T[K]*dnum_2 + P[bar]*dnum_3 | made entities are excluded from calculations in vertex if they | are included in the excluded phase list in the computational option | file (e.g., "in"); however, real entities to the right of the equals | sign in a make definition are not effected by the excluded phase list. | for example, if qL (liquid silica) is excluded, the make definition | q8L = 4 qL | will function, but qL will not be considered as a possible phase. | kyco silica buffer | kyco = 1 ky - 1 cor | 0 0 0 | sphene + cc + ru + q CO2 buffer | tcrq = 1 cc + 1 ru + 1 q - 1 sph | 0. 0. 0. | Ti phengite endmember for Auzanneau et al. (CMP 159:1-24, 2010) mica model | Gdqf corrected from -482876. to -13469.8 J/mol, D. Dolejs, Mar 6, 2010. | tip = 1 fcel + 1 geik - 1/2 fs | -13469.8 -14.694 .84 | mthm = 6 hem - 4 mt | mthm O2 buffer | 0 | qfm = 2 mt + 3 q -3 fa | qfm O2 buffer | 0 |emog = -1 fo - 2 gph + 1 mag + 1/2 en | EMOG O2 buffer |0 |ffm = -6 fa + 3 fs + 2 mt | ffm O2 buffer |0 |fff = 2 fa - 2 iron - 1 fs | iron fa fs O2 buffer |0 | tbi = 1 phl - 1 fo + 1 ru + 1 q | Ti-biotite endmember for TiBio(HP) model | 45e3 | tbi1 = 1 phl - 1 br + 1 ru | Ti-biotite endmember for TiBio(WPH) model | 78e3 | L Tajcamanova, 5/11/2006. | fbi = 1 east - 1/2 cor + 1/2 hem | Fe3+-biotite endmember for TiBio(WPH) model, definition corrected for | | presumed typo in the WPH (JMG, 2007) paper by L Tajcamanova, 5/11/2007. | 13.45e3 | fbi = 1 east - 1/2 cor + 1 hem, 8/10/2007, L Tajcamanova | Fe endmembers for ultramafic mineral solution | models, based on the talc Fe-Mg exchange. fbr = 1 br - 1/3 ta + 1/3 fta DQF(J/mol) = 0 fchum = 1 chum - 3 ta + 3 fta DQF(J/mol) = 0 fphA = 1 phA - 7/3 ta + 7/3 fta DQF(J/mol) = 0 fatg = 1 atg - 16 ta + 16 fta DQF(J/mol) = 0 atgts = 4 clin + 9/17 atg - 24/17 br | Tshermaks antigorite for Atg(PN) model (Padrón-Navarta et al., 2013, Lithos) DQF = -2e3 + 46.1*T_K | ettore's makes: | odo = 1/2 mag 1/2 cc | -1000. 0 0 | oank = 1/4 sid 1/2 cc 1/4 mag | -750 0 0 | odo = 1/2 mag + 1/2 cc | ordered dolmite species for H&P dolomite model | -13.5d3 | Green et al (2007) omphacite model, ds6 acm_dqf = 1 acm DQF(J/mol) = -7000 | Diener et al. (JMG, 2007) clinoamphibole model mrb = 1 gl - 2 jd +2 acm | magnesio riebekite, ds6, 3/7/18 JADC DQF(J/mol) = 0 ts_dqf = 1 ts | tschermakite DQF(J/mol) = 10000 parg_dqf = 1 parg | pargasite, ds6, 3/7/18 JADC DQF(J/mol) = -10000 gl_dqf = 1 gl | glaucophane, ds6, 3/7/18 JADC DQF(J/mol) = -3000 cumm_dqf = 1 cumm | ds6, 3/7/18 JADC DQF(J/mol) = 0 grun_dqf = 1 grun | ds6, 3/7/18 JADC DQF(J/mol) = -3000 | revised (Diener et al, JMG 2011 25:631-656) ortho-amphibole model. Oct 31, 2011. ogl_dqf = 1 gl | ortho-glaucophane DQF(J/mol) = 15000. fanth_dq = 1 fanth | ferro-anthophyllite DQF(J/mol) = 7000 omrb_dqf = 1 gl -2 jd +2 acm | ortho-magnesio riebekite (mrb dqf + 25000 J/mol), stoichiometry corrected 3/30/08 JADC DQF(J/mol) = 33000 mpa = 1 parg - 1 tr +1 anth DQF(J/mol) = 25d3 ged_dqf = 1 ged DQF(J/mol) = 20000 | make definition for coma of the unpublished | thermocalc scapolite model coma = 3 ab + 1 cc DQF(J/mol) = 25000. tbit = 1 phl - 1 br + 1 ru |Ti-Fe3+ Biotite after Tajcmanova et al. (2009) DQF(J/mol) = 84e3 -11.5 0 |Model entered by Lucie Tajcmanova, September, 2008. fbit = 1 east - 1/2 cor + 1/2 hem |Ti-Fe3+ Biotite after Tajcmanova et al. (2009) DQF(J/mol) = 6e3 0 0 | Make definitions for the Smye et al (JMG, 2011, 28:753-768) | models for Mica, Carpholite and Chloritoid, to use these | make definitions delete the leading "|" comment characters: ocar = 1 fcar + 1/2 hem - 1/2 cor DQF(J/mol) = 45d3 mncar = 1 mcar + 1 mang - 1 per | corrected from 1 mcar + 1 mang - 1/2 cor, G Hoschek, 10/24/11. DQF(J/mol) = 30d3 ma_dqf = 1 ma DQF(J/mol) = 3d3 | Make definition for the White et al (JMG, 2005) garnet, Gt(WPPH), JADC, 10/24/11. kho = 1 py - 1 gr + 1 andr DQF(J/mol) = 40d3 0 0 | Make definitions for the White et al (JMG, 2000) ilmenite, Ilm(WHP), JADC, 10/29/11. | Corrected coeffiecients for TC un-landau, formerly, the TC DQF was used without | modification. NOTE: the ilm and ilm_nol endmembers must be excluded from calculations | with the Ilm(WPH) model and the ilm_nol, oilm and dilm must be excluded from calculations | without the Ilm(WPH) model. JADC, 6/19/11. dilm = 1 ilm_nol | 1993 -2.1 0 => the TC DQF coeffecients, the values below are | oilm + {DH,R*ln(4),0} DQF(J/mol) = 17043.57559 -13.11797099 .1836386612e-1 dhem = 1 hem_nol DQF(J/mol) = 9.5228d3 -12.9377 T_K | Make definitions for Kelsey & Powell (JMG, 2011) Zr melting relations. JADC, 2/6/12 zr8L = 2 zrc | Zr-melt endmember DQF(J/mol) = 69e3 zrg = 1 gr + 3 zrc - 6 q | Zr garnet endmember DQF(J/mol) = 96e3 0.165e3 2.7 zrru = 1 bdy | Zr rutile endmember 52.84e3 -0.01829e3 -0.074 mots = 1 mgts - 1/2 cor + 1/2 hem | ferric opx endmember MgFe3+AlSiO6 for Opx(HP) 22d3 0 0 | Make definitions for White et al. (JMG 32:261-286, 2014) models f3clin = 1 clin - 1/2 gr + 1/2 andr DQF(J/mol) = 2d3 0 0 kho1 = 1 py - 1 gr + 1 andr DQF(J/mol) = 27d3 sil8L = 8/5 silL DQF(J/mol) = -23d3 fo8L = 2 foL DQF(J/mol) = -10d3 fa8L = 2 faL DQF(J/mol) = -9d3 0 -1.3 q8L = 4 qL DQF(J/mol) = -20 | a small DQF is added to stabilize q8L relative to qL fmu = 1 mu + 1/2 andr - 1/2 gr DQF(J/mol) = 25d3 ma1_dqf = 1 ma DQF(J/mol) = 6.5d3 ctdo = 1 mctd + 1/4 andr - 1/4 gr DQF(J/mol) = 25d3 msto = 1 andr -1 gr + 1 mst DQF(J/mol) = 9d3 mstt = 1 mst - 1 cor +3/2 ru DQF(J/mol) = 13d3 mots1 = 1 mgts + 1/2 andr - 1/2 gr DQF(J/mol) = 2d3 tbi = 1 phl - 1 br + 1 ru | Ti-biotite endmember for Bi(W) model DQF(J/mol) = 55e3 fbi = 1 east - 1/2 gr + 1/2 andr | Fe3+-biotite endmember for Bi(W) model DQF(J/mol) = -3e3 ospr = 1/2 andr - 1/2 gr + 1 spr5 DQF(J/mol) = -16d3 mnopx = 2 pxmn | Mn endmember for Opx(W) model DQF(J/mol) = 6680 | Make definitions for Jennings and Holland, J Pet, 56:869-892, 2015 Cpx cfs = 1 fs DQF(J/mol) = 3.8d3 -3 0.03 crdi = 1 cats + 1 kos - 1 jd DQF(J/mol) = -3d3 cess = 1 cats + 1 acm - 1 jd DQF(J/mol) = -6d3 cenjh = 1 en DQF(J/mol) = 3.5d3 - 2 * T_K + 0.048 * p_bar | Make definitions for Jennings and Holland, J Pet, 56:869-892, 2015 Opx cren = 1 mgts + 1 kos - 1 jd DQF(J/mol) = 3d3 oen = 1 mgts + 1 acm - 1 jd DQF(J/mol) = -15d3 + 0.15 * p_bar |odi = 1 di | DQF(J/mol) = -100 + 0.211 * T + 0.005 * P | dqf_T corrected from 2.11, ECRG 9/18 odi = 1 di | prior to 13/7/20: -100 + 0.211 * T + 0.005 * P | updated by ECRG, 13/7/20 DQF = 2800 + 0.005 * P | changed from DQF = 1900 + 0.005 * P by DB to match ECRG 10/20 revision | Make definitions for Jennings and Holland, J Pet, 56:869-892, 2015 melt qjL = 2 qL DQF(J/mol) = 4d3 - 0.43 * p_bar dijL = 1 diL DQF(J/mol) = -6.7d3 + 0.17 * p_bar jdjL = 1 abL - 1 qL | corrected 3/18/16, Oliver Shortle DQF(J/mol) = 18.7d3 - 0.16 * p_bar ctjL = 1 anL - 1 qL | corrected 3/18/16, Oliver Shortle DQF(J/mol) = 2.5d3 + 0.29 * p_bar fojL = 1 foL DQF(J/mol) = 2d3 - 0.03 * p_bar fajL = 1 faL DQF(J/mol) = -2.5d3 + 0.18 * p_bar hmjL = 0.5 hemL DQF(J/mol) = 0 + 0.20 * p_bar ekjL = 0.5 eskL DQF(J/mol) = 21d3 | Make definitions for Green et al., JMG, 2016 melt foTL = 2 foL dqf = -4d3 faTL = 2 faL dqf = -8.2d3 - 1.4 * P | Make definitions for Green et al., JMG, 2016 clinoamphibole mrbG = 1 gl - 1 gr + 1 andr DQF = 0 kprg = 1 mu - 1 pa + 1 parg DQF = -7060 + 20 * T_K tts = -2 dsp + 2 ru + 1 ts DQF = 95000 | Make definitions for Green et al., JMG, 2016 augite (clinopyroxene) cfsg = 1 fs DQF = 2100 - 2 * T + 0.045 * P | Make definitions for Holland et al., 2013; dx.doi.org/10.1093/petrology/egt035 | mantle mineralogical model. nacfb = 1 nacf DQF(J/mol) = -9000 mfpv = 1 fpv DQF(J/mol) = -9500 mcpv = 1 cpv DQF(J/mol) = 60000 mnpv = 1 npv DQF(J/mol) = 16000 cmpv = 1 mpv DQF(J/mol) = 35000 cfpv = 1 fpv DQF(J/mol) = 24000 capv = 1 apv DQF(J/mol) = 45000 cnpv = 1 npv DQF(J/mol) = 25000 fcor = 1 mcor + 1 fak - 1 mak | FeSi corundum DQF(J/mol) = -15d3 hmgts = 1 mgts + 1 hen - 1 en DQF(J/mol) = -1d3 |-------------------------------------------------------------------------------- | Make definitions for Holland et al., JPet, 2018 (HGP models) |--------------------------- Gt tig = 1 py + 1/2 per + 1/2 ru - 1/2 cor DQF(J/mol) = 46.7d3 - 17.3 * T |--------------------------- Sp isp = 1 nsp DQF(J/mol) = 23.6d3 - 5.76303 * T iherc = 1 nherc DQF(J/mol) = 23.6d3 - 5.76303 * T imt = 1 mt | changed to 30000 Aug 11, 2020, reverted to | original value, DB, Dec 2, 2020. DQF(J/mol) = 300 |--------------------------- Cpx cessh = 1 cats + 1 acm - 1 jd DQF = -3450 crdih = 1 cats + 1 kos - 1 jd DQF = -4900 mcbuf = 1 cats + 1/2 per + 1/2 ru -1/2 cor | corrected from -1750 ... 10/22/2019, Lisa Rummel, Mainz DQF = -16.2d3 - 1.2 * T - 0.005 * P | changed from DQF = 1750 - 1.2 * T - 0.005 * P by DB to match 10/20 ECRG revision kjdh = 1 jd + 1 san - 1 abh DQF = 11.7d3 + 0.6 * P | changed from DQF = -3750 + 1.189 * P by DB to match 10/20 ECRG revision |--------------------------- Opx, odi as in JH crenh = 1 mgts + 1 kos - 1 jd DQF = -25900 + 15.5 * T + 0.05 * P obuf = 1 mgts + 1/2 per + 1/2 ru - 1/2 cor DQF = -5000 - 5.1 * T - 0.0061 * P |changed from DQF = 3350 - 5.1 * T - 0.0061 * Pby DB to match 10/20 ECRG revision macm = 1 mgts + 1 acm - 1 jd DQF = 4800 - 0.089 * P ojd = 1 jd DQF = 18800 |--------------------------- high-density silicate melt, updated from the published | values to the values given in the TC files. JADC April 23, 2019. foHL = 2 foL dqf = 8.67d3 - 0.131*Pbar faHL = 2 faL dqf = 13.7d3 - 0.055*Pbar qHL = 4 qL dqf = 0.22d3 - 0.059*Pbar jdL = 1 abL - 1 qL dqf = 12.19d3 - 0.089*Pbar hmL = 1/2 hemL dqf = 3.3d3 - 0.032*Pbar ekL = 1/2 eskL dqf = 24.85d3 + 0.245*Pbar tiL = 1 ruL dqf = 5.58d3 - 0.489*Pbar kjL = 1 kspL - 1 qL dqf = 11.98d3 - 0.210*Pbar |--------------------------- low-density silicate-rich fluid/melt, updated from the published | values to the values given in the TC files. JADC April 23, 2019. foWL = 2 foL dqf = 8.59d3 - 0.136*Pbar faWL = 2 faL dqf = 13.56d3 - 0.052*Pbar qWL = 4 qL dqf = 2.1d3 - 0.051*Pbar jdWL = 1 abL - 1 qL dqf = 12.32d3 - 0.099*Pbar kWL = 1 kspL - 1 qL dqf = 12.88d3 - 0.227*Pbar hmWL = 1/2 hemL dqf = 4.05d3 - 0.077*Pbar ekWL = 1/2 eskL dqf = 24.75d3 + 0.245*Pbar tiWL = 1 ruL dqf = 5.6d3 - 0.489*Pbar |-------------------------------------------------------------------------------- | Make definitions for Tomlinson and Holland; JPet, 2021 (TH models) | Entered by Debaditya Bandyopadhyay, JADC 9/22 |--------------------------- Melt qTHL = 3 qL DQF(J/mol) = 0.47d3 - 0.078*Pbar foTHL = 2 foL DQF(J/mol) = 9.73d3 - 0.176*Pbar faTHL = 2 faL DQF(J/mol) = 16.52d3 - 0.034*Pbar neTHL = 1 abL - 2 qL DQF(J/mol) = 33.11d3 + 0.306*Pbar hmTHL = 1/2 hemL DQF(J/mol) = 3.76d3 - 0.027*Pbar ekTHL = 1/2 eskL DQF(J/mol) = 24.98d3 + 0.170*Pbar tiTHL = 1 ruL DQF(J/mol) = 0.42d3 - 0.257*Pbar kjTHL = 1 kspL - 1 qL DQF(J/mol) = 22.93d3 + 0.292*Pbar |--------------------------- Spinel | iherc and imt as in Sp(HGP) ispTH = 1 nsp DQF(J/mol) = 23.5d3 - 5.76303 * T |--------------------------- Garnet tigTH = 1 py + 1/2 per + 1/2 ru - 1/2 cor DQF(J/mol) = 53.5d3 - 17.3 * T |--------------------------- Opx | odi as in Opx(HGP) crenTH = 1 mgts + 1 kos - 1 jd DQF(J/mol) = -31850 + 15.5 * T + 0.05 * P obufTH = 1 mgts + 1/2 per + 1/2 ru - 1/2 cor DQF(J/mol) = 4350 - 5.1 * T - 0.0061 * P macmTH = 1 mgts + 1 acm - 1 jd DQF(J/mol) = 2630 - 0.089 * P ojdTH = 1 jd DQF(J/mol) = 18840 - 0.043 * P |--------------------------- Cpx | cenjh, cfsg as in Cpx(HGP) cessTH = 1 cats + 1 acm - 1 jd DQF(J/mol) = -5810 crdiTH = 1 cats + 1 kos - 1 jd DQF(J/mol) = -5660 mcbufTH = 1 cats + 1/2 per + 1/2 ru -1/2 cor DQF(J/mol) = -6.47d3 - 1.2 * T + 0.078 * P kjdTH = 1 jd + 1 san - 1 abh DQF(J/mol) = -4d3 + 1.35 * P end_makes Notation (incomplete and NOT alphabetical!) Entity Symbol Formula akermanite ak Ca2MgSi2O7 almandine alm Fe3Al2Si3O12 andalusite and Al2SiO5 andradite andr Ca3Fe2Si3O12 clinohumite chum Mg9Si4O16(OH)2 clinozoisite cz Ca2Al3Si3O12(OH) cordierite crd Mg2Al4Si5O18 epidote(ordered) ep Ca2FeAl2Si3O12(OH) fayalite fa Fe2SiO4 Fe-chloritoid fctd FeAl2SiO5(OH)2 Fe-cordierite fcrd Fe2Al4Si5O18 Fe-epidote fep Ca2Fe2AlSi3O12(OH) Fe-osumilite fosm KFe2Al5Si10O30 Fe-staurolite fst Fe4Al18Si7.5O48H4 forsterite fo Mg2SiO4 gehlenite geh Ca2Al2SiO7 grossular gr Ca3Al2Si3O12 hydrouscordierite hcrd Mg2Al4Si5O18H2O hydroxy-topaz tpz Al2SiO4(OH)2 kyanite ky Al2SiO5 larnite-bredigite larn Ca2SiO4 lawsonite law CaAl2Si2O7(OH)2H2O merwinite merw Ca3MgSi2O8 Mg-chloritoid mctd MgAl2SiO5(OH)2 Mg-staurolite mst Mg4Al18Si7.5O48H4 Mn-chloritoid mnctd MnAl2SiO5(OH)2 Mn-cordierite mncrd Mn2Al4Si5O18 Mn-staurolite mnst Mn4Al18Si7:5O48H4 monticellite mont CaMgSiO4 osumilite(1) osm1 KMg2Al5Si10O30 osumilite(2) osm2 KMg3Al3Si11O30 phase A phA Mg7Si2O8(OH)6 pumpellyite pump Ca4MgAl5Si6O21(OH)7 pyrope py Mg3Al2Si3O12 rankinite rnk Ca3Si2O7 sillimanite sill Al2SiO5 spessartine spss Mn3Al2Si3O12 sphene sph CaTiSiO5 spurrite spu Ca5Si2O8(CO3) tephroite teph Mn2SiO4 tilleyite ty Ca5Si2O7(CO3)2 vesuvianite vsv Ca19Mg2Al11Si18O69(OH)9 zircon zrc ZrSiO4 zoisite zo Ca2Al3Si3O12(OH) acmite acm NaFeSi2O6 Ca-tschermaks pyroxene cats CaAl2SiO6 Diopside di CaMgSi2O6 enstatite en Mg2Si2O6 ferrosilite fs Fe2Si2O6 hedenbergite hed CaFeSi2O6 jadeite jd NaAlSi2O6 mg-tschermak mgts MgAl2SiO6 pseudowollastonite pswo CaSiO3 pyroxmangite pxmn MnSiO3 rhodonite rhod MnSiO3 wollastonite wo CaSiO3 anthophyllite anth Mg7Si8O22(OH)2 cummingtonite cumm Mg7Si8O22(OH)2 Fe-anthophyllite fanth Fe7Si8O22(OH)2 Fe-glaucophane fgl Na2Fe3Al2Si8O22(OH)2 ferroactinolite ftr Ca2Fe5Si8O22(OH)2 gedrite(Na-free) ged Mg5Al4Si6O22(OH)2 glaucophane gl Na2Mg3Al2Si8O22(OH)2 grunerite grun Fe7Si8O22(OH)2 pargasite parg NaCa2Mg4Al3Si6O22(OH)2 riebeckite rieb Na2Fe5Si8O22(OH)2 tremolite tr Ca2Mg5Si8O22(OH)2 tschermakite ts Ca2Mg3Al4Si6O22(OH)2 deerite deer Fe18Si12O40(OH)10 fe-carpholite fcar FeAl2Si2O6(OH)4 fe-sapphirine(793) fspr Fe3.5Al9Si1.5O20 mg-carpholite mcar MgAl2Si2O6(OH)4 sapphirine(442) spr4 Mg4Al8Si2O20 sapphirine(793) spr7 Mg3.5Al9Si1.5O20 annite ann KFe3AlSi3O10(OH)2 celadonite cel KMgAlSi4O10(OH)2 eastonite east KMg2Al3Si2O10(OH)2 Fe-celadonite fcel KFeAlSi4O10(OH)2 margarite ma CaAl4Si2O10(OH)2 Mn-biotite mnbi KMn3AlSi3O10(OH)2 muscovite mu KAl3Si3O10(OH)2 Na-phlogopite naph NaMg3AlSi3O10(OH)2 paragonite pa NaAl3Si3O10(OH)2 phlogopite phl KMg3AlSi3O10(OH)2 Al-free chlorite afchl Mg6Si4O10(OH)8 amesite(14Ang) ames Mg4Al4Si2O10(OH)8 clinochlore(ordered) clin Mg5Al2Si3O10(OH)8 daphnite daph Fe5Al2Si3O10(OH)8 Fe-sudoite fsud Fe2Al4Si3O10(OH)8 Mn-chlorite mnchl Mn5Al2Si3O10(OH)8 Sudoite sud Mg2Al4Si3O10(OH)8 antigorite atg Mg48Si34O85(OH)62 chrysotile chr Mg3Si2O5(OH)2 Fe-talc fta Fe3Si4O10(OH)2 Kaolinite kao Al2Si2O5(OH)4 prehnite pre Ca2Al2Si3O10(OH)2 pyrophyllite prl Al2Si4O10(OH)2 talc ta Mg3Si4O10(OH)2 tschermak-talc tats Mg2Al2Si3O10(OH)2 albite ab NaAlSi3O8 analcite anl NaAlSi2O6H2O anorthite an CaAl2Si2O8 coesite coe SiO2 cristobalite crst SiO2 heulandite heu CaAl2Si7O186H2O highalbite abh NaAlSi3O8 kalsilite kals KAlSiO4 laumontite lmt CaAl2Si4O124H2O leucite lc KAlSi2O6 meionite me Ca4Al6Si6O24(CO3) microcline mic KAlSi3O8 nepheline ne NaAlSiO4 quartz q SiO2 sanidine san KAlSi3O8 stilbite stlb CaAl2Si7O187H2O stishovite stv SiO2 tridymite trd SiO2 wairakite wrk CaAl2Si4O12H2O3 baddeleyite bdy ZrO2 corundum cor Al2O3 geikielite geik MgTiO3 hematite hem Fe2O3 hercynite herc FeAl2O4 ilmenite ilm FeTiO3 lime lime CaO magnesioferrite mft MgFe2O4 magnetite mt Fe3O4 manganosite mang MnO nickel oxide NiO periclase per MgO pyrophanite pnt MnTiO3 rutile ru TiO2 spinel sp MgAl2O4 ulvospinel usp Fe2TiO4 brucite br Mg(OH)2 diaspore dsp AlO(OH) goethite gth FeO(OH) ankerite ank CaFe(CO3)2 aragonite arag CaCO3 calcite cc CaCO3 dolomite dol CaMg(CO3)2 magnesite mag MgCO3 rhodochrosite rhc MnCO3 siderite sid FeCO3 diamond diam C graphite gph C iron iron Fe nickel Ni Ni carbon dioxide CO2 carbon monoxide CO hydrogen H2 methane CH4 oxygen O2 water fluid H2O albite liquid abL NaAlSi3O8 anorthite liquid anL CaAl2Si2O8 diopside liquid diL CaMgSi2O6 enstatite liquid enL Mg2Si2O6 fayalite liquid faL Fe2SiO4 Fe-liquid (in KFMASH) fliq K3Fe5Al4Si19:5O47 Forsterite liquid foL Mg2SiO4 H2O liquid h2oL H2O H2O liquid (in KFMASH) hliq H2O K-feldspar liquid kspL KAlSi3O8 Mg liquid (in KFMASH) mliq K3Mg5Al4Si19:5O47 Silica liquid qL SiO2 Sillimanite liquid silL Al2SiO5 end fo EoS = 8 | H= -2172450 MgO(2)SiO2(1) GH = -2200804 S0 = 95.1 V0 = 4.366 c1 = 233.3 c2 = .1494E-2 c3 = -603800 c5 = -1869.7 b1 = .285E-4 b5 = 531.1171 b6 = 1285000 b7 = -.3E-5 b8 = 3.84 end fa EoS = 8 | H= -1477520 SiO2(1)FeO(2) GH = -1522541 S0 = 151 V0 = 4.631 c1 = 201.1 c2 = .1733E-1 c3 = -1960600 c5 = -900.9 b1 = .282E-4 b5 = 379.7022 b6 = 1256000 b7 = -.37E-5 b8 = 4.68 end teph EoS = 8 | H= -1733860 SiO2(1)MnO(2) GH = -1780342 S0 = 155.9 V0 = 4.899 c1 = 219.6 c3 = -1292700 c5 = -1308.3 b1 = .286E-4 b5 = 370.4448 b6 = 1256000 b7 = -.37E-5 b8 = 4.68 end lrn EoS = 8 | H= -2306860 SiO2(1)CaO(2) GH = -2344904 S0 = 127.6 V0 = 5.16 c1 = 247.5 c2 = -.3206E-2 c5 = -2051.9 b1 = .29E-4 b5 = 431.1559 b6 = 985000 b7 = -.41E-5 b8 = 4.07 transition = 1 type = 4 t1 = 1710 t2 = 10.03 t3 = .5E-1 end mont EoS = 8 | H= -2251160 MgO(1)SiO2(1)CaO(1) GH = -2283807 S0 = 109.5 V0 = 5.148 c1 = 250.7 c2 = -.10433E-1 c3 = -797200 c5 = -1996.1 b1 = .287E-4 b5 = 481.6406 b6 = 1134000 b7 = -.34E-5 b8 = 3.87 end chum EoS = 8 | H= -9613020 MgO(9)SiO2(4)H2O(1) GH = -9744355 S0 = 440.5 V0 = 19.801 c1 = 1071 c2 = -.16533E-1 c3 = -7899600 c5 = -7373.9 b1 = .32E-4 b5 = 537.4843 b6 = 1199000 b7 = -.38E-5 b8 = 4.58 end chdr EoS = 8 | H= -5254660 MgO(5)SiO2(2)H2O(1) GH = -5332179 S0 = 260 V0 = 11.084 c1 = 625 c2 = -.1088E-2 c3 = -2259900 c5 = -4910.7 b1 = .182E-4 b5 = 528.5176 b6 = 1161000 b7 = -.41E-5 b8 = 4.8 end mwd EoS = 8 | H= -2138030 MgO(2)SiO2(1) GH = -2166026 S0 = 93.9 V0 = 4.051 c1 = 208.7 c2 = .3942E-2 c3 = -1709500 c5 = -1302.8 b1 = .237E-4 b5 = 535.703 b6 = 1726000 b7 = -.22E-5 b8 = 3.84 end fwd EoS = 8 | H= -1467690 SiO2(1)FeO(2) GH = -1511220 S0 = 146 V0 = 4.321 c1 = 201.1 c2 = .1733E-1 c3 = -1960600 c5 = -900.9 b1 = .273E-4 b5 = 389.6378 b6 = 1690000 b7 = -.26E-5 b8 = 4.35 end mrw EoS = 8 | H= -2126780 MgO(2)SiO2(1) GH = -2153613 S0 = 90 V0 = 3.949 c1 = 213.3 c2 = .269E-2 c3 = -1410400 c5 = -1495.9 b1 = .201E-4 b5 = 551.1697 b6 = 1781000 b7 = -.24E-5 b8 = 4.35 end frw EoS = 8 | H= -1471520 SiO2(1)FeO(2) GH = -1513261 S0 = 140 V0 = 4.203 c1 = 166.8 c2 = .4261E-1 c3 = -1705400 c5 = -541.4 b1 = .222E-4 b5 = 402.2693 b6 = 1977000 b7 = -.25E-5 b8 = 4.92 end mpv EoS = 8 | H= -1442170 MgO(1)SiO2(1) GH = -1460834 S0 = 62.6 V0 = 2.445 c1 = 149.3 c2 = .2918E-2 c3 = -2983000 c5 = -799.1 b1 = .187E-4 b5 = 560.9705 b6 = 2510000 b7 = -.16E-5 b8 = 4.14 end fpv EoS = 8 | H= -1082710 SiO2(1)FeO(1) GH = -1111034 S0 = 95 V0 = 2.534 c1 = 133.2 c2 = .1083E-1 c3 = -3661400 c5 = -314.7 b1 = .187E-4 b5 = 418.0818 b6 = 2810000 b7 = -.16E-5 b8 = 4.14 end apv EoS = 8 | H= -1619610 Al2O3(1) GH = -1635054 S0 = 51.8 V0 = 2.54 c1 = 139.5 c2 = .589E-2 c3 = -2460600 c5 = -589.2 b1 = .18E-4 b5 = 633.0952 b6 = 2030000 b7 = -.2E-5 b8 = 4 end npv EoS = 8 | H= -1365000 Na2O(.25)Al2O3(.25)SiO2(1) GH = -1383783 S0 = 63 V0 = 2.334 c1 = 135 c2 = .846E-2 c3 = -1850300 c5 = -600.8 b1 = .18E-4 b5 = 558.6134 b6 = 2030000 b7 = -.2E-5 b8 = 4 end ppv EoS = 8 | H= -1418490 MgO(1)SiO2(1) GH = -1436498 S0 = 60.4 V0 = 2.442 c1 = 149.3 c2 = .2918E-2 c3 = -2983000 c5 = -799.1 b1 = .187E-4 b5 = 574.2981 b6 = 2312000 b7 = -.16E-5 b8 = 4 end cpv EoS = 8 | H= -1533530 SiO2(1)CaO(1) GH = -1555742 S0 = 74.5 V0 = 2.745 c1 = 159.3 c3 = -967300 c5 = -1075.4 b1 = .2E-4 b5 = 498.4067 b6 = 2360000 b7 = -.16E-5 b8 = 3.9 end mak EoS = 8 | H= -1489560 MgO(1)SiO2(1) GH = -1507240 S0 = 59.3 V0 = 2.635 c1 = 147.8 c2 = .2015E-2 c3 = -2395000 c5 = -801.8 b1 = .212E-4 b5 = 581.2022 b6 = 2110000 b7 = -.22E-5 b8 = 4.55 end fak EoS = 8 | H= -1142110 SiO2(1)FeO(1) GH = -1169391 S0 = 91.5 V0 = 2.76 c1 = 100.3 c2 = .13328E-1 c3 = -4364900 c5 = 419.8 b1 = .212E-4 b5 = 429.9111 b6 = 2180000 b7 = -.22E-5 b8 = 4.55 end maj EoS = 8 | H= -6041730 MgO(4)SiO2(4) GH = -6119309 S0 = 260.2 V0 = 11.457 c1 = 713.6 c2 = -.997E-3 c3 = -1158200 c5 = -6622.3 b1 = .183E-4 b5 = 546.838 b6 = 1600000 b7 = -.28E-5 b8 = 4.56 end nagt EoS = 8 | H= -5985000 Na2O(.5)MgO(2)Al2O3(.5)SiO2(4) GH = -6062698 S0 = 260.6 V0 = 11.09 c1 = 620.8 c2 = .112E-1 c3 = -3755900 c5 = -4421.3 b1 = .21E-4 b5 = 546.2763 b6 = 1700000 b7 = -.23E-5 b8 = 4 end py EoS = 8 | H= -6284620 MgO(3)Al2O3(1)SiO2(3) GH = -6364226 S0 = 267 V0 = 11.313 c1 = 633.5 c3 = -5196100 c5 = -4315.2 b1 = .237E-4 b5 = 537.4432 b6 = 1743000 b7 = -.23E-5 b8 = 4.05 end alm EoS = 8 | H= -5267570 Al2O3(1)SiO2(3)FeO(3) GH = -5367957 S0 = 336.7 V0 = 11.525 c1 = 716.2 c2 = -.1241E-1 c3 = -3160800 c5 = -5863.5 b1 = .212E-4 b5 = 456.971 b6 = 1900000 b7 = -.16E-5 b8 = 2.98 end spss EoS = 8 | H= -5692300 Al2O3(1)SiO2(3)MnO(3) GH = -5792270 S0 = 335.3 V0 = 11.792 c1 = 646.9 c3 = -4525800 c5 = -4452.8 b1 = .227E-4 b5 = 458.3495 b6 = 1740000 b7 = -.38E-5 b8 = 6.68 end gr EoS = 8 | H= -6642900 Al2O3(1)SiO2(3)CaO(3) GH = -6718928 S0 = 255 V0 = 12.535 c1 = 626 c3 = -5779200 c5 = -4002.9 b1 = .22E-4 b5 = 554.247 b6 = 1720000 b7 = -.32E-5 b8 = 5.53 end andr EoS = 8 | H= -5768850 SiO2(3)CaO(3)FeO(2)O2(.5) GH = -5863185 S0 = 316.4 V0 = 13.204 c1 = 638.6 c3 = -4955100 c5 = -3989.2 b1 = .286E-4 b5 = 477.8077 b6 = 1588000 b7 = -.36E-5 b8 = 5.68 end ski EoS = 8 | H= -4331140 SiO2(3)FeO(5)O2(.5) GH = -4451414 S0 = 403.4 V0 = 12.144 c1 = 689.9 c3 = -2948600 c5 = -5030.3 b1 = .285E-4 b5 = 399.6994 b6 = 1574000 b7 = -.43E-5 b8 = 6.7 end knor EoS = 8 | H= -5701120 MgO(3)SiO2(3)Cr2O3(1) GH = -5791161 S0 = 302 V0 = 11.738 c1 = 613 c2 = .3606E-2 c3 = -4178000 c5 = -3729.4 b1 = .237E-4 b5 = 493.779 b6 = 1534000 b7 = -.28E-5 b8 = 4.34 end uv EoS = 8 | H= -6057520 SiO2(3)CaO(3)Cr2O3(1) GH = -6153196 S0 = 320.9 V0 = 13.077 c1 = 605.1 c2 = .3606E-2 c3 = -4760600 c5 = -3417.1 b1 = .22E-4 b5 = 473.0265 b6 = 1620000 b7 = -.29E-5 b8 = 4.7 end osma EoS = 8 | H= -0.1489600E+08 MgO(2)Al2O3(2.5)SiO2(10)K2O(.5) GH = -.1512110E+08 S0 = 755 V0 = 37.893 c1 = 1540.7 c2 = -.11359E-1 c3 = -.1033900E+08 c5 = -11699 b1 = .47E-5 b5 = 479.7654 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 end osmm EoS = 8 | H= -0.1478628E+08 MgO(3)Al2O3(1.5)SiO2(11)K2O(.5) GH = -.1500691E+08 S0 = 740 V0 = 38.44 c1 = 1525.5 c2 = -.10267E-1 c3 = -.1053800E+08 c5 = -11337 b1 = .47E-5 b5 = 486.625 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 end osfa EoS = 8 | H= -0.1421533E+08 Al2O3(2.5)SiO2(10)K2O(.5)FeO(2) GH = -.1444789E+08 S0 = 780 V0 = 38.45 c1 = 1558.6 c2 = -.11359E-1 c3 = -9476500 c5 = -11845 b1 = .49E-5 b5 = 468.7528 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 end vsv EoS = 8 | H= -0.4234518E+08 MgO(2)Al2O3(5.5)SiO2(18)CaO(19)H2O(4.5) GH = -.4290868E+08 S0 = 1890 V0 = 85.2 c1 = 4488 c2 = -.57952E-1 c3 = -.2226930E+08 c5 = -33478 b1 = .275E-4 b5 = 525.6078 b6 = 1255000 b7 = -.38E-5 b8 = 4.8 end and EoS = 8 | H= -2588560 Al2O3(1)SiO2(1) GH = -2616199 S0 = 92.7 V0 = 5.153 c1 = 277.3 c2 = -.6588E-2 c3 = -1914100 c5 = -2265.6 b1 = .181E-4 b5 = 589.9875 b6 = 1442000 b7 = -.48E-5 b8 = 6.89 end ky EoS = 8 | H= -2592860 Al2O3(1)SiO2(1) GH = -2617756 S0 = 83.5 V0 = 4.414 c1 = 279.4 c2 = -.7124E-2 c3 = -2055600 c5 = -2289.4 b1 = .192E-4 b5 = 630.1881 b6 = 1601000 b7 = -.25E-5 b8 = 4.05 end sill EoS = 8 | H= -2585660 Al2O3(1)SiO2(1) GH = -2614104 S0 = 95.4 V0 = 4.986 c1 = 280.2 c2 = -.69E-2 c3 = -1375700 c5 = -2399.4 b1 = .112E-4 b5 = 579.1451 b6 = 1640000 b7 = -.31E-5 b8 = 5.06 transition = 1 type = 5 t1 = 4750 t2 = .1E-1 t3 = 4750 t4 = .1E-1 t5 = 1 t6 = .25 end smul EoS = 8 | H= -2569210 Al2O3(1)SiO2(1) GH = -2599472 S0 = 101.5 V0 = 4.987 c1 = 280.2 c2 = -.69E-2 c3 = -1375700 c5 = -2399.4 b1 = .136E-4 b5 = 556.058 b6 = 1740000 b7 = -.23E-5 b8 = 4 end amul EoS = 8 | H= -2485870 Al2O3(1.25)SiO2(.5) GH = -2519561 S0 = 113 V0 = 5.083 c1 = 244.8 c2 = .968E-3 c3 = -2533300 c5 = -1641.6 b1 = .136E-4 b5 = 505.9788 b6 = 1740000 b7 = -.23E-5 b8 = 4 end tpz EoS = 8 | H= -2898700 Al2O3(1)SiO2(1)H2O(1) GH = -2928664 S0 = 100.5 V0 = 5.339 c1 = 351.7 c2 = -.112E-1 c3 = -3908000 c5 = -2511.8 b1 = .157E-4 b5 = 682.8295 b6 = 1315000 b7 = -.31E-5 b8 = 4.06 end mst EoS = 8 | H= -0.2512257E+08 MgO(4)Al2O3(9)SiO2(7.5)H2O(2) GH = -.2539389E+08 S0 = 910 V0 = 44.26 c1 = 2820.5 c2 = -.59366E-1 c3 = -.1377400E+08 c5 = -24126 b1 = .181E-4 b5 = 604.1244 b6 = 1684000 b7 = -.24E-5 b8 = 4.05 end fst EoS = 8 | H= -0.2375528E+08 Al2O3(9)SiO2(7.5)FeO(4)H2O(2) GH = -.2405641E+08 S0 = 1010 V0 = 44.88 c1 = 2880 c2 = -.56595E-1 c3 = -.1064200E+08 c5 = -25373 b1 = .183E-4 b5 = 564.7642 b6 = 1800000 b7 = -.26E-5 b8 = 4.76 end mnst EoS = 8 | H= -0.2424230E+08 Al2O3(9)SiO2(7.5)MnO(4)H2O(2) GH = -.2455059E+08 S0 = 1034 V0 = 45.46 c1 = 2873.3 c2 = -.89064E-1 c3 = -.1268800E+08 c5 = -24749 b1 = .209E-4 b5 = 556.0692 b6 = 1800000 b7 = -.26E-5 b8 = 4.76 end mctd EoS = 8 | H= -3549140 MgO(1)Al2O3(1)SiO2(1)H2O(1) GH = -3592670 S0 = 146 V0 = 6.875 c1 = 417.4 c2 = -.3771E-2 c3 = -2920600 c5 = -3417.8 b1 = .263E-4 b5 = 601.898 b6 = 1456000 b7 = -.28E-5 b8 = 4.06 end fctd EoS = 8 | H= -3208540 Al2O3(1)SiO2(1)FeO(1)H2O(1) GH = -3258331 S0 = 167 V0 = 6.98 c1 = 416.1 c2 = -.3477E-2 c3 = -2835900 c5 = -3360.3 b1 = .28E-4 b5 = 551.4837 b6 = 1456000 b7 = -.28E-5 b8 = 4.06 end mnctd EoS = 8 | H= -3335440 Al2O3(1)SiO2(1)MnO(1)H2O(1) GH = -3384933 S0 = 166 V0 = 7.175 c1 = 464.4 c2 = -.12654E-1 c3 = -1147200 c5 = -4341 b1 = .26E-4 b5 = 553.6921 b6 = 1456000 b7 = -.28E-5 b8 = 4.06 end merw EoS = 8 | H= -4545540 MgO(1)SiO2(2)CaO(3) GH = -4621002 S0 = 253.1 V0 = 9.847 c1 = 417.5 c2 = .8117E-2 c3 = -2923000 c5 = -2320.3 b1 = .319E-4 b5 = 433.7936 b6 = 1200000 b7 = -.34E-5 b8 = 4.07 end spu EoS = 8 | H= -5846590 SiO2(2)CaO(5)CO2(1) GH = -5945576 S0 = 332 V0 = 14.697 c1 = 614.1 c2 = -.3508E-2 c3 = -2493100 c5 = -4168 b1 = .34E-4 b5 = 444.7663 b6 = 950000 b7 = -.43E-5 b8 = 4.09 end zo EoS = 8 | H= -6896170 Al2O3(1.5)SiO2(3)CaO(2)H2O(.5) GH = -6985019 S0 = 298 V0 = 13.575 c1 = 662 c2 = .10416E-1 c3 = -6006400 c5 = -4260.7 b1 = .312E-4 b5 = 532.187 b6 = 1044000 b7 = -.38E-5 b8 = 4 end cz EoS = 8 | H= -6895410 Al2O3(1.5)SiO2(3)CaO(2)H2O(.5) GH = -6985153 S0 = 301 V0 = 13.63 c1 = 630.9 c2 = .13693E-1 c3 = -6645800 c5 = -3731.1 b1 = .233E-4 b5 = 528.5805 b6 = 1197000 b7 = -.34E-5 b8 = 4.07 end ep EoS = 8 | H= -6473670 Al2O3(1)SiO2(3)CaO(2)FeO(1)O2(.25)H2O(.5) GH = -6567587 S0 = 315 V0 = 13.92 c1 = 613.3 c2 = .2207E-1 c3 = -7160000 c5 = -2987.7 b1 = .234E-4 b5 = 512.3763 b6 = 1340000 b7 = -.3E-5 b8 = 4 end fep EoS = 8 | H= -6028040 Al2O3(.5)SiO2(3)CaO(2)FeO(2)O2(.5)H2O(.5) GH = -6126131 S0 = 329 V0 = 14.21 c1 = 584.7 c2 = .30447E-1 c3 = -7674200 c5 = -2244.3 b1 = .231E-4 b5 = 497.1361 b6 = 1513000 b7 = -.26E-5 b8 = 4 end pmt EoS = 8 | H= -6542560 Al2O3(1)SiO2(3)CaO(2)MnO(1)O2(.25)H2O(.5) GH = -6643931 S0 = 340 V0 = 13.82 c1 = 569.8 c2 = .2779E-1 c3 = -5442900 c5 = -2812.6 b1 = .238E-4 b5 = 485.7831 b6 = 1197000 b7 = -.34E-5 b8 = 4.07 end law EoS = 8 | H= -4868570 Al2O3(1)SiO2(2)CaO(1)H2O(2) GH = -4936846 S0 = 229 V0 = 10.132 c1 = 687.8 c2 = .1566E-2 c3 = 375900 c5 = -7179.2 b1 = .265E-4 b5 = 575.148 b6 = 1229000 b7 = -.44E-5 b8 = 5.45 end mpm EoS = 8 | H= -0.1438661E+08 MgO(1)Al2O3(2.5)SiO2(6)CaO(4)H2O(3.5) GH = -.1457415E+08 S0 = 629 V0 = 29.55 c1 = 1720.8 c2 = -.24928E-1 c3 = -5998700 c5 = -14620.3 b1 = .248E-4 b5 = 566.5483 b6 = 1615000 b7 = -.25E-5 b8 = 4.05 end fpm EoS = 8 | H= -0.1403411E+08 Al2O3(2.5)SiO2(6)CaO(4)FeO(1)H2O(3.5) GH = -.1422999E+08 S0 = 657 V0 = 29.68 c1 = 1737.2 c2 = -.24582E-1 c3 = -5161100 c5 = -14963 b1 = .249E-4 b5 = 550.4506 b6 = 1615000 b7 = -.25E-5 b8 = 4.05 end jgd EoS = 8 | H= -0.1180884E+08 SiO2(6)CaO(4)FeO(6)O2(1.25)H2O(3.5) GH = -.1205630E+08 S0 = 830 V0 = 31.08 c1 = 1795.4 c2 = -.37986E-1 c3 = -4455700 c5 = -14888 b1 = .249E-4 b5 = 468.247 b6 = 1615000 b7 = -.25E-5 b8 = 4.05 end geh EoS = 8 | H= -3992130 Al2O3(1)SiO2(1)CaO(2) GH = -4051313 S0 = 198.5 V0 = 9.024 c1 = 405.7 c2 = -.7099E-2 c3 = -1188300 c5 = -3174.4 b1 = .223E-4 b5 = 462.8037 b6 = 1080000 b7 = -.38E-5 b8 = 4.08 transition = 1 type = 5 t1 = 7510 t2 = .9E-1 t3 = 7500 t4 = .9E-1 t5 = 1 t6 = .8 end ak EoS = 8 | H= -3865490 MgO(1)SiO2(2)CaO(2) GH = -3928847 S0 = 212.5 V0 = 9.254 c1 = 385.4 c2 = .3209E-2 c3 = -247500 c5 = -2889.9 b1 = .257E-4 b5 = 440.4445 b6 = 1420000 b7 = -.29E-5 b8 = 4.06 end rnk EoS = 8 | H= -3943740 SiO2(2)CaO(3) GH = -4006351 S0 = 210 V0 = 9.651 c1 = 372.3 c2 = -.2893E-2 c3 = -2462400 c5 = -2181.3 b1 = .328E-4 b5 = 444.2774 b6 = 950000 b7 = -.43E-5 b8 = 4.09 end ty EoS = 8 | H= -6367930 SiO2(2)CaO(5)CO2(2) GH = -6484208 S0 = 390 V0 = 17.039 c1 = 741.7 c2 = -.5345E-2 c3 = -1434600 c5 = -5878.5 b1 = .342E-4 b5 = 440.0993 b6 = 950000 b7 = -.43E-5 b8 = 4.09 end crd EoS = 8 | H= -9163130 MgO(2)Al2O3(2)SiO2(5) GH = -9283612 S0 = 404.1 V0 = 23.322 c1 = 906.1 c3 = -7902000 c5 = -6293.4 b1 = .68E-5 b5 = 522.0255 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 transition = 1 type = 5 t1 = 36710 t2 = .1 t3 = 36700 t4 = .1 t5 = 2 t6 = 1.5 end hcrd EoS = 8 | H= -9448140 MgO(2)Al2O3(2)SiO2(5)H2O(1) GH = -9592146 S0 = 483 V0 = 23.322 c1 = 955.3 c3 = -8352600 c5 = -6301.2 b1 = .67E-5 b5 = 493.9223 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 transition = 1 type = 5 t1 = 36710 t2 = .1 t3 = 36700 t4 = .1 t5 = 2 t6 = 1.5 end fcrd EoS = 8 | H= -8444000 Al2O3(2)SiO2(5)FeO(2) GH = -8581447 S0 = 461 V0 = 23.71 c1 = 924 c3 = -7039400 c5 = -6439.6 b1 = .67E-5 b5 = 476.1702 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 transition = 1 type = 5 t1 = 36710 t2 = .1 t3 = 36700 t4 = .1 t5 = 2 t6 = 1.5 end mncrd EoS = 8 | H= -8692110 Al2O3(2)SiO2(5)MnO(2) GH = -8833135 S0 = 473 V0 = 24.027 c1 = 886.5 c3 = -8840000 c5 = -5590.4 b1 = .69E-5 b5 = 467.5094 b6 = 1290000 b7 = -.31E-5 b8 = 4.1 transition = 1 type = 5 t1 = 36710 t2 = .1 t3 = 36700 t4 = .1 t5 = 2 t6 = 1.5 end phA EoS = 8 | H= -7129510 MgO(7)SiO2(2)H2O(3) GH = -7234012 S0 = 350.5 V0 = 15.422 c1 = 962 c2 = -.11521E-1 c3 = -4517800 c5 = -7724.7 b1 = .355E-4 b5 = 574.1056 b6 = 1450000 b7 = -.28E-5 b8 = 4.06 end phD EoS = 8 | H= -2670130 MgO(1)SiO2(2)H2O(1) GH = -2703284 S0 = 111.2 V0 = 5.103 c1 = 294.6 c2 = .7944E-2 c3 = -5008700 c5 = -1335.5 b1 = .379E-4 b5 = 642.6939 b6 = 1650000 b7 = -.3E-5 b8 = 5 end phE EoS = 8 | H= -2931120 MgO(2.4)SiO2(1.2)H2O(1.2) GH = -2981507 S0 = 169 V0 = 6.435 c1 = 397.4 c2 = -.3533E-2 c3 = -1344400 c5 = -3290.2 b1 = .379E-4 b5 = 518.2394 b6 = 930000 b7 = -.54E-5 b8 = 5 end shB EoS = 8 | H= -9477280 MgO(10)SiO2(3)H2O(2) GH = -9595347 S0 = 396 V0 = 18.615 c1 = 1077.7 c2 = .642E-3 c3 = -7407400 c5 = -7428.7 b1 = .356E-4 b5 = 599.0666 b6 = 1320000 b7 = -.391E-5 b8 = 5.3 end sph EoS = 8 | H= -2596810 SiO2(1)CaO(1)TiO2(1) GH = -2635331 S0 = 129.2 V0 = 5.565 c1 = 227.9 c2 = .2924E-2 c3 = -3539500 c5 = -894.3 b1 = .158E-4 b5 = 470.8278 b6 = 1017000 b7 = -.97E-5 b8 = 9.85 transition = 1 type = 4 t1 = 485 t2 = .4 t3 = .5E-2 end cstn EoS = 8 | H= -2482850 SiO2(2)CaO(1) GH = -2512516 S0 = 99.5 V0 = 4.818 c1 = 205.6 c2 = .6034E-2 c3 = -5517700 c5 = -352.6 b1 = .158E-4 b5 = 563.4221 b6 = 1782000 b7 = -.22E-5 b8 = 4 end zrc EoS = 8 | H= -2035160 SiO2(1)ZrO2(1) GH = -2059915 S0 = 83.03 V0 = 3.926 c1 = 232 c2 = -.14405E-1 c5 = -2238.2 b1 = .125E-4 b5 = 524.5007 b6 = 2301000 b7 = -.18E-5 b8 = 4.04 end zrt EoS = 8 | H= -1993600 TiO2(1)ZrO2(1) GH = -2024250 S0 = 102.8 V0 = 4.42 c1 = 214.6 c2 = -.8226E-2 c3 = 190300 c5 = -1820.4 b1 = .125E-4 b5 = 451.1878 b6 = 2301000 b7 = -.18E-5 b8 = 4.04 end tcn EoS = 8 | H= -1763150 SiO2(1)TiO2(1) GH = -1787300 S0 = 81 V0 = 3.493 c1 = 208.6 c2 = -.3669E-2 c3 = 113000 c5 = -1906.9 b1 = .125E-4 b5 = 533.4002 b6 = 2301000 b7 = -.18E-5 b8 = 4.04 end en EoS = 8 | H= -3089930 MgO(2)SiO2(2) GH = -3129435 S0 = 132.5 V0 = 6.262 c1 = 356.2 c2 = -.299E-2 c3 = -596900 c5 = -3185.3 b1 = .227E-4 b5 = 540.1727 b6 = 1059000 b7 = -.82E-5 b8 = 8.65 end pren EoS = 8 | H= -3084260 MgO(2)SiO2(2) GH = -3125107 S0 = 137 V0 = 6.476 c1 = 356.2 c2 = -.299E-2 c3 = -596900 c5 = -3185.3 b1 = .23E-4 b5 = 528.1033 b6 = 1059000 b7 = -.82E-5 b8 = 8.65 end cen EoS = 8 | H= -3090810 MgO(2)SiO2(2) GH = -3130166 S0 = 132 V0 = 6.264 c1 = 306 c2 = -.3793E-2 c3 = -3041700 c5 = -1852.1 b1 = .211E-4 b5 = 541.5479 b6 = 1059000 b7 = -.82E-5 b8 = 8.65 end hen EoS = 8 | H= -3082430 MgO(2)SiO2(2) GH = -3121696 S0 = 131.7 V0 = 6.099 c1 = 356.2 c2 = -.299E-2 c3 = -596900 c5 = -3185.3 b1 = .226E-4 b5 = 542.3763 b6 = 1500000 b7 = -.36E-5 b8 = 5.5 end hfs EoS = 8 | H= -2380570 SiO2(2)FeO(2) GH = -2436920 S0 = 189 V0 = 6.405 c1 = 398.7 c2 = -.6579E-2 c3 = 1290100 c5 = -4058 b1 = .237E-4 b5 = 419.7316 b6 = 1500000 b7 = -.36E-5 b8 = 5.5 end fs EoS = 8 | H= -2388520 SiO2(2)FeO(2) GH = -2445139 S0 = 189.9 V0 = 6.592 c1 = 398.7 c2 = -.6579E-2 c3 = 1290100 c5 = -4058 b1 = .326E-4 b5 = 418.2462 b6 = 1010000 b7 = -.4E-5 b8 = 4.08 end mgts EoS = 8 | H= -3200570 MgO(1)Al2O3(1)SiO2(1) GH = -3238882 S0 = 128.5 V0 = 6.05 c1 = 371.4 c2 = -.4082E-2 c3 = -398400 c5 = -3547.1 b1 = .217E-4 b5 = 551.3738 b6 = 1028000 b7 = -.83E-5 b8 = 8.55 end di EoS = 8 | H= -3201760 MgO(1)SiO2(2)CaO(1) GH = -3244366 S0 = 142.9 V0 = 6.619 c1 = 314.5 c2 = .41E-4 c3 = -2745900 c5 = -2020.1 b1 = .273E-4 b5 = 513.0728 b6 = 1192000 b7 = -.44E-5 b8 = 5.19 end hed EoS = 8 | H= -2841970 SiO2(2)CaO(1)FeO(1) GH = -2894146 S0 = 175 V0 = 6.795 c1 = 340.2 c2 = .812E-3 c3 = -1047800 c5 = -2646.7 b1 = .238E-4 b5 = 444.2774 b6 = 1192000 b7 = -.33E-5 b8 = 3.97 end jd EoS = 8 | H= -3025360 Na2O(.5)Al2O3(.5)SiO2(2) GH = -3065163 S0 = 133.5 V0 = 6.04 c1 = 319.4 c2 = .3616E-2 c3 = -1173900 c5 = -2469.5 b1 = .21E-4 b5 = 537.4432 b6 = 1281000 b7 = -.3E-5 b8 = 3.81 end kjd EoS = 8 | H= -2932700 Al2O3(.5)SiO2(2)K2O(.5) GH = -2974811 S0 = 141.24 V0 = 6.479 c1 = 316.2 c2 = .6905E-2 c3 = -905300 c5 = -2489 b1 = .273E-4 b5 = 517.2145 b6 = 1450000 b7 = -.34E-5 b8 = 5 end acm EoS = 8 | H= -2583310 Na2O(.5)SiO2(2)FeO(1)O2(.25) GH = -2634174 S0 = 170.6 V0 = 6.459 c1 = 307.1 c2 = .16758E-1 c3 = -1685500 c5 = -2125.8 b1 = .211E-4 b5 = 452.5957 b6 = 1060000 b7 = -.38E-5 b8 = 4.08 end kos EoS = 8 | H= -2744890 Na2O(.5)SiO2(2)Cr2O3(.5) GH = -2789508 S0 = 149.65 V0 = 6.309 c1 = 309.2 c2 = .5419E-2 c3 = -664600 c5 = -2176.6 b1 = .194E-4 b5 = 496.8932 b6 = 1308000 b7 = -.23E-5 b8 = 3 end cats EoS = 8 | H= -3310020 Al2O3(1)SiO2(1)CaO(1) GH = -3350270 S0 = 135 V0 = 6.356 c1 = 347.6 c2 = -.6974E-2 c3 = -1781600 c5 = -2757.5 b1 = .208E-4 b5 = 533.4002 b6 = 1192000 b7 = -.44E-5 b8 = 5.19 transition = 1 type = 5 t1 = 3800 t2 = .1E-1 t3 = 3800 t4 = .1E-1 t5 = 1 t6 = .25 end caes EoS = 8 | H= -2997680 Al2O3(.5)SiO2(2)CaO(.5) GH = -3034531 S0 = 123.6 V0 = 6.05 c1 = 358.2 c2 = -.10213E-1 c3 = -880500 c5 = -3352.2 b1 = .231E-4 b5 = 546.8232 b6 = 1192000 b7 = -.44E-5 b8 = 5.19 end rhod EoS = 8 | H= -1322280 SiO2(1)MnO(1) GH = -1352244 S0 = 100.5 V0 = 3.494 c1 = 138.4 c2 = .4088E-2 c3 = -1936000 c5 = -538.9 b1 = .281E-4 b5 = 400.7536 b6 = 840000 b7 = -.48E-5 b8 = 4 end pxmn EoS = 8 | H= -1323070 SiO2(1)MnO(1) GH = -1352676 S0 = 99.3 V0 = 3.472 c1 = 138.4 c2 = .4088E-2 c3 = -1936000 c5 = -538.9 b1 = .28E-4 b5 = 404.4106 b6 = 840000 b7 = -.48E-5 b8 = 4 end wo EoS = 8 | H= -1633740 SiO2(1)CaO(1) GH = -1658337 S0 = 82.5 V0 = 3.993 c1 = 159.3 c3 = -967300 c5 = -1075.4 b1 = .254E-4 b5 = 463.6443 b6 = 795000 b7 = -.52E-5 b8 = 4.1 end pswo EoS = 8 | H= -1627940 SiO2(1)CaO(1) GH = -1654118 S0 = 87.8 V0 = 4.008 c1 = 157.8 c3 = -967300 c5 = -1075.4 b1 = .285E-4 b5 = 443.1667 b6 = 1100000 b7 = -.37E-5 b8 = 4.08 end wal EoS = 8 | H= -1625570 SiO2(1)CaO(1) GH = -1650764 S0 = 84.5 V0 = 3.7633 c1 = 159.3 c3 = -967300 c5 = -1075.4 b1 = .32E-4 b5 = 455.6984 b6 = 860000 b7 = -.47E-5 b8 = 4 end tr EoS = 8 | H= -0.1230422E+08 MgO(5)SiO2(8)CaO(2)H2O(1) GH = -.1246910E+08 S0 = 553 V0 = 27.27 c1 = 1260.2 c2 = .383E-2 c3 = -.1145500E+08 c5 = -8237.6 b1 = .261E-4 b5 = 533.7266 b6 = 762000 b7 = -.54E-5 b8 = 4.1 end ftr EoS = 8 | H= -0.1050350E+08 SiO2(8)CaO(2)FeO(5)H2O(1) GH = -.1071519E+08 S0 = 710 V0 = 28.42 c1 = 1290 c2 = .29992E-1 c3 = -8447500 c5 = -8947 b1 = .288E-4 b5 = 447.6982 b6 = 760000 b7 = -.54E-5 b8 = 4.1 end ts EoS = 8 | H= -0.1255386E+08 MgO(3)Al2O3(2)SiO2(6)CaO(2)H2O(1) GH = -.1271277E+08 S0 = 533 V0 = 26.739 c1 = 1244.8 c2 = .24348E-1 c3 = -.1196500E+08 c5 = -8112.1 b1 = .266E-4 b5 = 547.1193 b6 = 760000 b7 = -.54E-5 b8 = 4.1 end parg EoS = 8 | H= -0.1266463E+08 Na2O(.5)MgO(4)Al2O3(1.5)SiO2(6)CaO(2)H2O(1) GH = -.1285396E+08 S0 = 635 V0 = 27.19 c1 = 1280.2 c2 = .22997E-1 c3 = -.1235950E+08 c5 = -8065.8 b1 = .28E-4 b5 = 493.3428 b6 = 912000 b7 = -.45E-5 b8 = 4.09 end gl EoS = 8 | H= -0.1195586E+08 Na2O(1)MgO(3)Al2O3(1)SiO2(8)H2O(1) GH = -.1211388E+08 S0 = 530 V0 = 25.98 c1 = 1717.5 c2 = -.12107 c3 = 7075000 c5 = -19272 b1 = .158E-4 b5 = 549.1864 b6 = 883000 b7 = -.46E-5 b8 = 4.09 end fgl EoS = 8 | H= -0.1087951E+08 Na2O(1)Al2O3(1)SiO2(8)FeO(3)H2O(1) GH = -.1106556E+08 S0 = 624 V0 = 26.59 c1 = 1762.9 c2 = -.118992 c3 = 9423700 c5 = -20207.1 b1 = .183E-4 b5 = 491.0545 b6 = 890000 b7 = -.46E-5 b8 = 4.09 end nyb EoS = 8 | H= -0.1216533E+08 Na2O(1.5)MgO(3)Al2O3(1.5)SiO2(7)H2O(1) GH = -.1235078E+08 S0 = 622 V0 = 26.314 c1 = 1745.2 c2 = -.112162 c3 = 6425500 c5 = -19163 b1 = .22E-4 b5 = 500.5289 b6 = 910000 b7 = -.45E-5 b8 = 4.09 end rieb EoS = 8 | H= -0.1002405E+08 Na2O(1)SiO2(8)FeO(5)O2(.5)H2O(1) GH = -.1023126E+08 S0 = 695 V0 = 27.49 c1 = 1787.3 c2 = -.124882 c3 = 9627100 c5 = -20275.5 b1 = .181E-4 b5 = 454.7005 b6 = 890000 b7 = -.46E-5 b8 = 4.09 end anth EoS = 8 | H= -0.1206579E+08 MgO(7)SiO2(8)H2O(1) GH = -.1222590E+08 S0 = 537 V0 = 26.54 c1 = 1277.3 c2 = .25825E-1 c3 = -9704600 c5 = -9074.7 b1 = .252E-4 b5 = 544.3873 b6 = 700000 b7 = -.59E-5 b8 = 4.11 end fanth EoS = 8 | H= -9623830 SiO2(8)FeO(7)H2O(1) GH = -9839989 S0 = 725 V0 = 27.87 c1 = 1383.1 c2 = .30669E-1 c3 = -4224700 c5 = -11257.6 b1 = .274E-4 b5 = 440.9084 b6 = 700000 b7 = -.59E-5 b8 = 4.11 end cumm EoS = 8 | H= -0.1206364E+08 MgO(7)SiO2(8)H2O(1) GH = -.1222404E+08 S0 = 538 V0 = 26.33 c1 = 1277.3 c2 = .25825E-1 c3 = -9704600 c5 = -9074.7 b1 = .252E-4 b5 = 543.7085 b6 = 700000 b7 = -.59E-5 b8 = 4.11 end grun EoS = 8 | H= -9606390 SiO2(8)FeO(7)H2O(1) GH = -9825530 S0 = 735 V0 = 27.84 c1 = 1383.1 c2 = .30669E-1 c3 = -4224700 c5 = -11257.6 b1 = .274E-4 b5 = 436.495 b6 = 648000 b7 = -.64E-5 b8 = 4.12 end ged EoS = 8 | H= -0.1230655E+08 MgO(5)Al2O3(2)SiO2(6)H2O(1) GH = -.1246606E+08 S0 = 535 V0 = 25.956 c1 = 1307.7 c2 = .23642E-1 c3 = -9307400 c5 = -9799 b1 = .241E-4 b5 = 545.7499 b6 = 700000 b7 = -.59E-5 b8 = 4.11 end spr4 EoS = 8 | H= -0.1101989E+08 MgO(4)Al2O3(4)SiO2(2) GH = -.1114675E+08 S0 = 425.5 V0 = 19.9 c1 = 1133.1 c2 = -.7596E-2 c3 = -8816600 c5 = -8180.6 b1 = .205E-4 b5 = 561.1271 b6 = 2500000 b7 = -.16E-5 b8 = 4.04 end spr5 EoS = 8 | H= -0.1113452E+08 MgO(3)Al2O3(5)SiO2(1) GH = -.1125959E+08 S0 = 419.5 V0 = 19.75 c1 = 1103.4 c2 = .1015E-2 c3 = -.1095700E+08 c5 = -7409.2 b1 = .206E-4 b5 = 566.4004 b6 = 2500000 b7 = -.16E-5 b8 = 4.04 end fspr EoS = 8 | H= -9657660 Al2O3(4)SiO2(2)FeO(4) GH = -9802263 S0 = 485 V0 = 19.923 c1 = 1132.9 c2 = -.7348E-2 c3 = -.1042020E+08 c5 = -7036.6 b1 = .196E-4 b5 = 513.6996 b6 = 2500000 b7 = -.17E-5 b8 = 4.04 end mcar EoS = 8 | H= -4770910 MgO(1)Al2O3(1)SiO2(2)H2O(2) GH = -4836950 S0 = 221.5 V0 = 10.59 c1 = 683 c2 = -.14054E-1 c3 = 291000 c5 = -6976.4 b1 = .243E-4 b5 = 587.6927 b6 = 525000 b7 = -.79E-5 b8 = 4.14 end fcar EoS = 8 | H= -4411670 Al2O3(1)SiO2(2)FeO(1)H2O(2) GH = -4486535 S0 = 251.1 V0 = 10.695 c1 = 686.6 c2 = -.12415E-1 c3 = 186000 c5 = -6884 b1 = .221E-4 b5 = 541.1128 b6 = 525000 b7 = -.79E-5 b8 = 4.14 end deer EoS = 8 | H= -0.1833978E+08 SiO2(12)FeO(18)O2(1.5)H2O(5) GH = -.1883173E+08 S0 = 1650 V0 = 55.74 c1 = 3164.4 c2 = -.27883E-1 c3 = -5039100 c5 = -26721 b1 = .275E-4 b5 = 429.3326 b6 = 630000 b7 = -.65E-5 b8 = 4.12 end mu EoS = 8 | H= -5976520 Al2O3(1.5)SiO2(3)K2O(.5)H2O(1) GH = -6063580 S0 = 292 V0 = 14.083 c1 = 756.4 c2 = -.1984E-1 c3 = -2170000 c5 = -6979.2 b1 = .307E-4 b5 = 522.7881 b6 = 490000 b7 = -.85E-5 b8 = 4.15 end cel EoS = 8 | H= -5834980 MgO(1)Al2O3(.5)SiO2(4)K2O(.5)H2O(1) GH = -5921443 S0 = 290 V0 = 13.957 c1 = 741.2 c2 = -.18748E-1 c3 = -2368800 c5 = -6616.9 b1 = .307E-4 b5 = 525.2469 b6 = 700000 b7 = -.59E-5 b8 = 4.11 end fcel EoS = 8 | H= -5468880 Al2O3(.5)SiO2(4)K2O(.5)FeO(1)H2O(1) GH = -5567269 S0 = 330 V0 = 14.07 c1 = 756.3 c2 = -.19147E-1 c3 = -1586100 c5 = -6928.7 b1 = .318E-4 b5 = 480.0877 b6 = 700000 b7 = -.59E-5 b8 = 4.11 end pa EoS = 8 | H= -5942650 Na2O(.5)Al2O3(1.5)SiO2(3)H2O(1) GH = -6025238 S0 = 277 V0 = 13.211 c1 = 803 c2 = -.3158E-1 c3 = 217000 c5 = -8151 b1 = .37E-4 b5 = 541.8106 b6 = 515000 b7 = -.126E-4 b8 = 6.51 end ma EoS = 8 | H= -6241920 Al2O3(2)SiO2(2)CaO(1)H2O(1) GH = -6320930 S0 = 265 V0 = 12.964 c1 = 744.4 c2 = -.168E-1 c3 = -2074400 c5 = -6783.2 b1 = .233E-4 b5 = 558.0552 b6 = 1000000 b7 = -.41E-5 b8 = 4.08 end phl EoS = 8 | H= -6214560 MgO(3)Al2O3(.5)SiO2(3)K2O(.5)H2O(1) GH = -6311757 S0 = 326 V0 = 14.964 c1 = 770.3 c2 = -.36939E-1 c3 = -2328900 c5 = -6531.6 b1 = .38E-4 b5 = 500.325 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end ann EoS = 8 | H= -5141040 Al2O3(.5)SiO2(3)K2O(.5)FeO(3)H2O(1) GH = -5266263 S0 = 420 V0 = 15.432 c1 = 815.7 c2 = -.34861E-1 c3 = 19800 c5 = -7466.7 b1 = .38E-4 b5 = 416.5931 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end fbi EoS = 8 | H= -5896080 MgO(2)Al2O3(1)SiO2(2)K2O(.5)FeO(1)O2(.25)H2O(1) GH = -6000045 S0 = 348.7 V0 = 15.0725 c1 = 791.8 c2 = -.38031E-1 c3 = -1718300 c5 = -6886.9 b1 = .38E-4 b5 = 477.1646 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end obi EoS = 8 | H= -5862620 MgO(2)Al2O3(.5)SiO2(3)K2O(.5)FeO(1)H2O(1) GH = -5969158 S0 = 357.33 V0 = 15.12 c1 = 785.4 c2 = -.36246E-1 c3 = -1546000 c5 = -6843.3 b1 = .38E-4 b5 = 468.9124 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end mnbi EoS = 8 | H= -5475440 Al2O3(.5)SiO2(3)K2O(.5)MnO(3)H2O(1) GH = -5604539 S0 = 433 V0 = 15.264 c1 = 809.9 c2 = -.59213E-1 c3 = -1514400 c5 = -6998.7 b1 = .38E-4 b5 = 407.1692 b6 = 530000 b7 = -.143E-4 b8 = 7.33 end east EoS = 8 | H= -6329980 MgO(2)Al2O3(1.5)SiO2(2)K2O(.5)H2O(1) GH = -6424792 S0 = 318 V0 = 14.738 c1 = 785.5 c2 = -.38031E-1 c3 = -2130300 c5 = -6893.7 b1 = .38E-4 b5 = 509.0324 b6 = 530000 b7 = -.143E-4 b8 = 7.33 end naph EoS = 8 | H= -6164580 Na2O(.5)MgO(3)Al2O3(.5)SiO2(3)H2O(1) GH = -6259392 S0 = 318 V0 = 14.45 c1 = 773.5 c2 = -.40229E-1 c3 = -2597900 c5 = -6512.6 b1 = .328E-4 b5 = 509.0324 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end |tan EoS = 8 | H= -5899750 |MgO(3)SiO2(4)H2O(1) |GH = -5976971 S0 = 259 V0 = 13.665 |c1 = 622.2 c3 = -6385500 c5 = -3916.3 |b1 = .18E-4 b5 = 566.5483 b6 = 430000 b7 = -.144E-4 b8 = 6.17 |end clin EoS = 8 | H= -8908790 MgO(5)Al2O3(1)SiO2(3)H2O(4) GH = -9039082 S0 = 437 V0 = 21.14 c1 = 1170.8 c2 = -.1508E-2 c3 = -3825800 c5 = -10315 b1 = .204E-4 b5 = 572.4777 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end ames EoS = 8 | H= -9039760 MgO(4)Al2O3(2)SiO2(2)H2O(4) GH = -9162598 S0 = 412 V0 = 20.71 c1 = 1186 c2 = -.2599E-2 c3 = -3627200 c5 = -10677 b1 = .2E-4 b5 = 594.7068 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end afchl EoS = 8 | H= -8727820 MgO(6)SiO2(4)H2O(4) GH = -8858708 S0 = 439 V0 = 21.57 c1 = 1155 c2 = -.417E-3 c3 = -4024400 c5 = -9952.9 b1 = .204E-4 b5 = 570.771 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end daph EoS = 8 | H= -7118390 Al2O3(1)SiO2(3)FeO(5)H2O(4) GH = -7292510 S0 = 584 V0 = 21.62 c1 = 1192 c2 = -.594E-2 c3 = -4826400 c5 = -9768.3 b1 = .227E-4 b5 = 469.3273 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end mnchl EoS = 8 | H= -7698970 Al2O3(1)SiO2(3)MnO(5)H2O(4) GH = -7876369 S0 = 595 V0 = 22.59 c1 = 1136.5 c2 = -.5243E-2 c3 = -5548100 c5 = -8911.5 b1 = .223E-4 b5 = 463.0835 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end sud EoS = 8 | H= -8626320 MgO(2)Al2O3(2)SiO2(3)H2O(4) GH = -8744089 S0 = 395 V0 = 20.3 c1 = 1436.1 c2 = -.48749E-1 c3 = -2748500 c5 = -13764 b1 = .199E-4 b5 = 600.0322 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end fsud EoS = 8 | H= -7900370 Al2O3(2)SiO2(3)FeO(2)H2O(4) GH = -8036326 S0 = 456 V0 = 20.4 c1 = 1466.3 c2 = -.47365E-1 c3 = -1182800 c5 = -14388 b1 = .208E-4 b5 = 546.3164 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end prl EoS = 8 | H= -5640640 Al2O3(1)SiO2(4)H2O(1) GH = -5711898 S0 = 239 V0 = 12.804 c1 = 784.5 c2 = -.42948E-1 c3 = 1251000 c5 = -8495.9 b1 = .45E-4 b5 = 578.3578 b6 = 370000 b7 = -.271E-4 b8 = 10 end ta EoS = 8 | H= -5896700 MgO(3)SiO2(4)H2O(1) GH = -5973921 S0 = 259 V0 = 13.665 c1 = 622.2 c3 = -6385500 c5 = -3916.3 b1 = .18E-4 b5 = 566.5483 b6 = 430000 b7 = -.144E-4 b8 = 6.17 end fta EoS = 8 | H= -4799140 SiO2(4)FeO(3)H2O(1) GH = -4904089 S0 = 352 V0 = 14.225 c1 = 579.7 c2 = .39494E-1 c3 = -6459300 c5 = -3088.1 b1 = .18E-4 b5 = 458.4106 b6 = 430000 b7 = -.144E-4 b8 = 6.17 end tats EoS = 8 | H= -6000790 MgO(2)Al2O3(1)SiO2(3)H2O(1) GH = -6078011 S0 = 259 V0 = 13.51 c1 = 549.5 c2 = .36324E-1 c3 = -8606600 c5 = -2515.3 b1 = .18E-4 b5 = 566.5483 b6 = 430000 b7 = -.144E-4 b8 = 6.17 end |tap EoS = 8 | H= -5649530 |Al2O3(1)SiO2(4)H2O(1) |GH = -5719595 S0 = 235 V0 = 13.45 |c1 = 784.5 c2 = -.42948E-1 c3 = 1251000 c5 = -8495.9 |b1 = .45E-4 b5 = 584.7169 b6 = 370000 b7 = -.271E-4 b8 = 10 |end |nta EoS = 8 | H= -6163410 |Na2O(.5)MgO(3)Al2O3(.5)SiO2(3)H2O(1) |GH = -6258222 S0 = 318 V0 = 14.45 |c1 = 773.5 c2 = -.40229E-1 c3 = -2597900 c5 = -6512.6 |b1 = .328E-4 b5 = 509.0324 b6 = 513000 b7 = -.143E-4 b8 = 7.33 |end minn EoS = 8 | H= -4818890 SiO2(4)FeO(3)H2O(1) GH = -4924733 S0 = 355 V0 = 14.851 c1 = 579.7 c2 = .39494E-1 c3 = -6459300 c5 = -3088.1 b1 = .18E-4 b5 = 455.6054 b6 = 430000 b7 = -.144E-4 b8 = 6.17 end minm EoS = 8 | H= -5865700 MgO(3)SiO2(4)H2O(1) GH = -5944382 S0 = 263.9 V0 = 14.291 c1 = 622.2 c3 = -6385500 c5 = -3916.3 b1 = .18E-4 b5 = 559.5931 b6 = 430000 b7 = -.144E-4 b8 = 6.17 end kao EoS = 8 | H= -4122080 Al2O3(1)SiO2(2)H2O(2) GH = -4182813 S0 = 203.7 V0 = 9.934 c1 = 436.7 c2 = -.34295E-1 c3 = -4055900 c5 = -2699.1 b1 = .251E-4 b5 = 577.3421 b6 = 645000 b7 = -.64E-5 b8 = 4.12 end pre EoS = 8 | H= -6202040 Al2O3(1)SiO2(3)CaO(2)H2O(1) GH = -6289338 S0 = 292.8 V0 = 14.026 c1 = 724.9 c2 = -.13865E-1 c3 = -2059000 c5 = -6323.9 b1 = .158E-4 b5 = 521.811 b6 = 1093000 b7 = -.37E-5 b8 = 4.01 end fpre EoS = 8 | H= -5766470 Al2O3(.5)SiO2(3)CaO(2)FeO(1)O2(.25)H2O(1) GH = -5861878 S0 = 320 V0 = 14.8 c1 = 737.1 c2 = -.1681E-1 c3 = -1957300 c5 = -6358.1 b1 = .158E-4 b5 = 490.6335 b6 = 1093000 b7 = -.37E-5 b8 = 4.01 end chr EoS = 8 | H= -4360720 MgO(3)SiO2(2)H2O(2) GH = -4426701 S0 = 221.3 V0 = 10.746 c1 = 624.7 c2 = -.2077E-1 c3 = -1721800 c5 = -5619.4 b1 = .22E-4 b5 = 567.7243 b6 = 628000 b7 = -.64E-5 b8 = 4 end liz EoS = 8 | H= -4368910 MgO(3)SiO2(2)H2O(2) GH = -4432118 S0 = 212 V0 = 10.645 c1 = 614.7 c2 = -.2077E-1 c3 = -1721800 c5 = -5619.4 b1 = .22E-4 b5 = 583.8253 b6 = 710000 b7 = -.45E-5 b8 = 3.2 end glt EoS = 8 | H= -3297370 SiO2(2)FeO(3)H2O(2) GH = -3389796 S0 = 310 V0 = 11.98 c1 = 576.4 c2 = .2984E-2 c3 = -3757000 c5 = -4166.2 b1 = .228E-4 b5 = 449.4929 b6 = 630000 b7 = -.63E-5 b8 = 4 end fstp EoS = 8 | H= -0.1255093E+08 Al2O3(1)SiO2(8)K2O(.25)FeO(5)H2O(6.25) GH = -.1282827E+08 S0 = 930.2 V0 = 37.239 c1 = 1944.3 c2 = -.12289E-1 c3 = -4840200 c5 = -16635 b1 = .368E-4 b5 = 476.0785 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end mstp EoS = 8 | H= -0.1428640E+08 MgO(5)Al2O3(1)SiO2(8)K2O(.25)H2O(6.25) GH = -.1453905E+08 S0 = 847.4 V0 = 36.577 c1 = 1862.2 c2 = -.14018E-1 c3 = -8983100 c5 = -14923 b1 = .371E-4 b5 = 508.2801 b6 = 513000 b7 = -.143E-4 b8 = 7.33 end atg EoS = 8 | H= -0.7139994E+08 MgO(48)SiO2(34)H2O(31) GH = -.7247924E+08 S0 = 3620 V0 = 175.48 c1 = 9621 c2 = -.91183E-1 c3 = -.3594160E+08 c5 = -83034.2 b1 = .28E-4 b5 = 563.3516 b6 = 631000 b7 = -.94E-5 b8 = 5.92 end ab EoS = 8 | H= -3935300 Na2O(.5)Al2O3(.5)SiO2(3) GH = -3997136 S0 = 207.4 V0 = 10.067 c1 = 452 c2 = -.13364E-1 c3 = -1275900 c5 = -3953.6 b1 = .236E-4 b5 = 474.9519 b6 = 541000 b7 = -.109E-4 b8 = 5.91 transition = 1 type = 5 t1 = 14000 t2 = .42E-1 t3 = 13000 t4 = .42E-1 t5 = 3 t6 = .9 end abh EoS = 8 | H= -3921300 Na2O(.5)Al2O3(.5)SiO2(3) GH = -3988175 S0 = 224.3 V0 = 10.105 c1 = 452 c2 = -.13364E-1 c3 = -1275900 c5 = -3953.6 b1 = .241E-4 b5 = 448.8929 b6 = 541000 b7 = -.109E-4 b8 = 5.91 end |mic EoS = 8 | H= -3975420 |Al2O3(.5)SiO2(3)K2O(.5) |GH = -4039314 S0 = 214.3 V0 = 10.871 |c1 = 448.8 c2 = -.10075E-1 c3 = -1007300 c5 = -3973.1 |b1 = .166E-4 b5 = 463.9554 b6 = 583000 b7 = -.69E-5 b8 = 4.02 |end san EoS = 8 | H= -3966770 Al2O3(.5)SiO2(3)K2O(.5) GH = -4030664 S0 = 214.3 V0 = 10.871 c1 = 448.8 c2 = -.10075E-1 c3 = -1007300 c5 = -3973.1 b1 = .166E-4 b5 = 463.9554 b6 = 583000 b7 = -.69E-5 b8 = 4.02 transition = 1 type = 5 t1 = 8650 t2 = .24E-1 t3 = 8500 t4 = .24E-1 t5 = 3 t6 = .8 end an EoS = 8 | H= -4232630 Al2O3(1)SiO2(2)CaO(1) GH = -4292409 S0 = 200.5 V0 = 10.079 c1 = 370.5 c2 = .1001E-1 c3 = -4339100 c5 = -1960.6 b1 = .141E-4 b5 = 486.4823 b6 = 860000 b7 = -.48E-5 b8 = 4.09 transition = 1 type = 5 t1 = 42010 t2 = .1 t3 = 42000 t4 = .1 t5 = 1 t6 = 2 end kcm EoS = 8 | H= -4232710 Al2O3(.5)SiO2(3)K2O(.5)H2O(1) GH = -4316639 S0 = 281.5 V0 = 11.438 c1 = 536.5 c2 = -.1009E-1 c3 = -980400 c5 = -4735 b1 = .321E-4 b5 = 442.5443 b6 = 425000 b7 = -.47E-5 b8 = 2 end wa EoS = 8 | H= -4272000 SiO2(4)K2O(1) GH = -4347730 S0 = 254 V0 = 10.844 c1 = 499.1 c5 = -4350.1 b1 = .266E-4 b5 = 455.0485 b6 = 900000 b7 = -.44E-5 b8 = 4 end hol EoS = 8 | H= -3792040 Al2O3(.5)SiO2(3)K2O(.5) GH = -3841593 S0 = 166.2 V0 = 7.128 c1 = 417.6 c2 = -.3617E-2 c3 = -4748100 c5 = -2819.9 b1 = .28E-4 b5 = 553.249 b6 = 1800000 b7 = -.22E-5 b8 = 4 end q EoS = 8 | H= -910650.0 SiO2(1) GH = -923002.4 S0 = 41.43 V0 = 2.269 c1 = 92.8 c2 = -.642E-3 c3 = -714900 c5 = -716.1 b5 = 525.2346 b6 = 584000 b7 = -.153E-4 b8 = 8.96 transition = 1 type = 4 t1 = 847 t2 = 5.35 t3 = .1267 end trd EoS = 8 | H= -907010.0 SiO2(1) GH = -920188.2 S0 = 44.2 V0 = 2.8 c1 = 74.9 c2 = .31E-2 c3 = -1174000 c5 = -236.7 b5 = 502.33 b6 = 150000 b7 = -.291E-4 b8 = 4.36 end crst EoS = 8 | H= -904170.0 SiO2(1) GH = -919363.7 S0 = 50.96 V0 = 2.745 c1 = 72.7 c2 = .1304E-2 c3 = -4129000 b5 = 454.0125 b6 = 160000 b7 = -.272E-4 b8 = 4.35 end coe EoS = 8 | H= -907000.0 SiO2(1) GH = -918836.6 S0 = 39.7 V0 = 2.064 c1 = 107.8 c2 = -.3279E-2 c3 = -190300 c5 = -1041.6 b1 = .123E-4 b5 = 540.6303 b6 = 979000 b7 = -.43E-5 b8 = 4.19 end stv EoS = 8 | H= -876770.0 SiO2(1) GH = -883925.6 S0 = 24 V0 = 1.401 c1 = 68.1 c2 = .601E-2 c3 = -1978200 c5 = -82.1 b1 = .158E-4 b5 = 736.5651 b6 = 3090000 b7 = -.15E-5 b8 = 4.6 end ne EoS = 8 | H= -2094850 Na2O(.5)Al2O3(.5)SiO2(1) GH = -2131940 S0 = 124.4 V0 = 5.419 c1 = 272.7 c2 = -.12398E-1 c5 = -2763.1 b1 = .463E-4 b5 = 439.2967 b6 = 465000 b7 = -.89E-5 b8 = 4.16 transition = 1 type = 4 t1 = 467 t2 = 10 t3 = .8E-1 end cg EoS = 8 | H= -2092020 Na2O(.5)Al2O3(.5)SiO2(1) GH = -2127410 S0 = 118.7 V0 = 5.603 c1 = 116.1 c2 = .86021E-1 c3 = -1992700 b1 = .45E-4 b5 = 454.5854 b6 = 465000 b7 = -.89E-5 b8 = 4.16 end cgh EoS = 8 | H= -2078300 Na2O(.5)Al2O3(.5)SiO2(1) GH = -2118550 S0 = 135 V0 = 5.67 c1 = 229.2 c2 = .11876E-1 c5 = -1970.7 b1 = .467E-4 b5 = 413.4385 b6 = 465000 b7 = -.89E-5 b8 = 4.16 end macf EoS = 8 | H= -2246340 MgO(1)Al2O3(1) GH = -2270192 S0 = 80 V0 = 3.614 c1 = 200 c2 = .6252E-2 c3 = -2996400 c5 = -888.4 b1 = .193E-4 b5 = 595.235 b6 = 2120000 b7 = -.17E-5 b8 = 4 end mscf EoS = 8 | H= -2061500 MgO(2)SiO2(1) GH = -2087588 S0 = 87.5 V0 = 3.649 c1 = 213.3 c2 = .269E-2 c3 = -1410400 c5 = -1495.9 b1 = .201E-4 b5 = 561.5628 b6 = 1850000 b7 = -.17E-5 b8 = 4 end fscf EoS = 8 | H= -1402500 SiO2(1)FeO(2) GH = -1445255 S0 = 143.4 V0 = 3.914 c1 = 181.1 c2 = .18526E-1 c3 = -2767200 c5 = -527.1 b1 = .201E-4 b5 = 395.0127 b6 = 1850000 b7 = -.17E-5 b8 = 4 end nacf EoS = 8 | H= -1965620 Na2O(.5)Al2O3(.5)SiO2(1) GH = -1998416 S0 = 110 V0 = 3.631 c1 = 272.7 c2 = -.12398E-1 c5 = -2763.1 b1 = .21E-4 b5 = 480.0877 b6 = 1850000 b7 = -.25E-5 b8 = 4.6 end cacf EoS = 8 | H= -2325600 Al2O3(1)CaO(1) GH = -2351718 S0 = 87.6 V0 = 3.976 c1 = 191.9 c2 = .9563E-2 c3 = -3211300 c5 = -640.2 b1 = .193E-4 b5 = 561.1396 b6 = 1900000 b7 = -.21E-5 b8 = 4 end manal EoS = 8 | H= -6796630 MgO(3)Al2O3(3) GH = -6871167 S0 = 250 V0 = 11.166 c1 = 600 c2 = .18756E-1 c3 = -8989200 c5 = -2665.2 b1 = .193E-4 b5 = 579.784 b6 = 1840000 b7 = -.22E-5 b8 = 4 end nanal EoS = 8 | H= -6610270 Na2O(.5)MgO(2)Al2O3(2.5)SiO2(1) GH = -6693752 S0 = 280 V0 = 11.322 c1 = 672.7 c2 = .106E-3 c3 = -5992800 c5 = -4539.9 b1 = .201E-4 b5 = 537.8962 b6 = 1840000 b7 = -.22E-5 b8 = 4 end msnal EoS = 8 | H= -6172380 MgO(6)SiO2(3) GH = -6253626 S0 = 272.5 V0 = 11.061 c1 = 639.9 c2 = .807E-2 c3 = -4231200 c5 = -4487.7 b1 = .21E-4 b5 = 547.7903 b6 = 1850000 b7 = -.22E-5 b8 = 4 end fsnal EoS = 8 | H= -4146000 SiO2(3)FeO(6) GH = -4277246 S0 = 440.2 V0 = 11.856 c1 = 543.3 c2 = .55578E-1 c3 = -8301600 c5 = -1581.3 b1 = .21E-4 b5 = 388.1482 b6 = 1850000 b7 = -.22E-5 b8 = 4 end canal EoS = 8 | H= -6840000 MgO(2)Al2O3(3)CaO(1) GH = -6916803 S0 = 257.6 V0 = 11.159 c1 = 591.9 c2 = .22067E-1 c3 = -9204100 c5 = -2417 b1 = .193E-4 b5 = 568.5674 b6 = 1770000 b7 = -.22E-5 b8 = 4 end sdl EoS = 8 | H= -0.1340731E+08 Na2O(4)Al2O3(3)SiO2(6)Cl2(1)O2(-.5) GH = -.1367863E+08 S0 = 910 V0 = 42.13 c1 = 1532.7 c2 = .47747E-1 c3 = -2972800 c5 = -12427 b1 = .463E-4 b5 = 405.6042 b6 = 465000 b7 = -.89E-5 b8 = 4.16 end kls EoS = 8 | H= -2123130 Al2O3(.5)SiO2(1)K2O(.5) GH = -2163678 S0 = 136 V0 = 6.052 c1 = 242 c2 = -.4482E-2 c3 = -895800 c5 = -1935.8 b1 = .316E-4 b5 = 411.1553 b6 = 514000 b7 = -.39E-5 b8 = 2 end lc EoS = 8 | H= -3029400 Al2O3(.5)SiO2(2)K2O(.5) GH = -3088583 S0 = 198.5 V0 = 8.826 c1 = 369.8 c2 = -.16332E-1 c3 = 684700 c5 = -3683.1 b1 = .185E-4 b5 = 404.5645 b6 = 450000 b7 = -.127E-4 b8 = 5.7 transition = 1 type = 5 t1 = 11610 t2 = .4 t3 = 11600 t4 = .4 t5 = 2 t6 = .7 end me EoS = 8 | H= -0.1384162E+08 Al2O3(3)SiO2(6)CaO(4)CO2(1) GH = -.1406583E+08 S0 = 752 V0 = 33.985 c1 = 1359 c2 = .36442E-1 c3 = -8594700 c5 = -9598.2 b1 = .182E-4 b5 = 452.0012 b6 = 870000 b7 = -.47E-5 b8 = 4.09 end wrk EoS = 8 | H= -6662250 Al2O3(1)SiO2(4)CaO(1)H2O(2) GH = -6775547 S0 = 380 V0 = 19.04 c1 = 838.3 c2 = -.2146E-1 c3 = -2272000 c5 = -7292.3 b1 = .149E-4 b5 = 491.4972 b6 = 860000 b7 = -.48E-5 b8 = 4.09 end lmt EoS = 8 | H= -7262500 Al2O3(1)SiO2(4)CaO(1)H2O(4) GH = -7401140 S0 = 465 V0 = 20.37 c1 = 1013.4 c2 = -.21413E-1 c3 = -2235800 c5 = -8806.7 b1 = .137E-4 b5 = 496.0821 b6 = 860000 b7 = -.48E-5 b8 = 4.09 end heu EoS = 8 | H= -0.1054482E+08 Al2O3(1)SiO2(7)CaO(1)H2O(6) GH = -.1077827E+08 S0 = 783 V0 = 31.7 c1 = 1504.8 c2 = -.33224E-1 c3 = -2959300 c5 = -13297.2 b1 = .157E-4 b5 = 453.3338 b6 = 274000 b7 = -.146E-4 b8 = 4 end stlb EoS = 8 | H= -0.1089637E+08 Al2O3(1)SiO2(7)CaO(1)H2O(7) GH = -.1110806E+08 S0 = 710 V0 = 32.87 c1 = 1588.4 c2 = -.32043E-1 c3 = -3071600 c5 = -13966.9 b1 = .151E-4 b5 = 508.175 b6 = 860000 b7 = -.48E-5 b8 = 4.09 end anl EoS = 8 | H= -3307110 Na2O(.5)Al2O3(.5)SiO2(2)H2O(1) GH = -3376281 S0 = 232 V0 = 9.74 c1 = 643.5 c2 = -.16067E-1 c3 = 9302300 c5 = -9179.6 b1 = .276E-4 b5 = 437.945 b6 = 400000 b7 = -.104E-4 b8 = 4.18 end lime EoS = 8 | H= -634570.0 CaO(1) GH = -645929.5 S0 = 38.1 V0 = 1.676 c1 = 52.4 c2 = .3673E-2 c3 = -750700 c5 = -51 b1 = .341E-4 b5 = 417.2617 b6 = 1130000 b7 = -.34E-5 b8 = 3.87 end ru EoS = 8 | H= -943770.0 TiO2(1) GH = -958856.4 S0 = 50.6 V0 = 1.882 c1 = 80.9 c2 = .1658E-2 c3 = -1243900 c5 = -211.1 b1 = .224E-4 b5 = 456.3501 b6 = 2220000 b7 = -.19E-5 b8 = 4.24 end per EoS = 8 | H= -601600.0 MgO(1) GH = -609501 S0 = 26.5 V0 = 1.125 c1 = 60.5 c2 = .362E-3 c3 = -535800 c5 = -299.2 b1 = .311E-4 b5 = 540.1727 b6 = 1616000 b7 = -.24E-5 b8 = 3.95 end fper EoS = 8 | H= -262150.0 FeO(1) GH = -279621.6 S0 = 58.6 V0 = 1.206 c1 = 44.4 c2 = .828E-2 c3 = -1214200 c5 = 185.2 b1 = .322E-4 b5 = 297.5937 b6 = 1520000 b7 = -.32E-5 b8 = 4.9 end wu EoS = 8 | H= -262440.0 FeO(1) GH = -281223.4 S0 = 63 V0 = 1.206 c1 = 67.4 c2 = .3758E-2 c3 = 315700 c5 = -381.7 b1 = .322E-4 b5 = 280.3374 b6 = 1520000 b7 = -.32E-5 b8 = 4 end mang EoS = 8 | H= -385580.0 MnO(1) GH = -403379.6 S0 = 59.7 V0 = 1.322 c1 = 59.8 c2 = .36E-2 c3 = -31400 c5 = -282.6 b1 = .369E-4 b5 = 293.0835 b6 = 1645000 b7 = -.27E-5 b8 = 4.46 end cor EoS = 8 | H= -1675190 Al2O3(1) GH = -1690366 S0 = 50.9 V0 = 2.558 c1 = 139.5 c2 = .589E-2 c3 = -2460600 c5 = -589.2 b1 = .18E-4 b5 = 639.9519 b6 = 2540000 b7 = -.17E-5 b8 = 4.34 end mcor EoS = 8 | H= -1468450 MgO(1)SiO2(1) GH = -1486130 S0 = 59.3 V0 = 2.635 c1 = 147.8 c2 = .2015E-2 c3 = -2395000 c5 = -801.8 b1 = .212E-4 b5 = 581.2022 b6 = 2110000 b7 = -.22E-5 b8 = 4.55 end hem EoS = 8 | H= -825430.0 FeO(2)O2(.5) GH = -851488.3 S0 = 87.4 V0 = 3.027 c1 = 163.9 c3 = -2257200 c5 = -657.6 b1 = .279E-4 b5 = 444.6488 b6 = 2230000 b7 = -.18E-5 b8 = 4.04 transition = 1 type = 4 t1 = 955 t2 = 15.6 end esk EoS = 8 | H= -1128170 Cr2O3(1) GH = -1152916 S0 = 83 V0 = 2.898 c1 = 119 c2 = .9496E-2 c3 = -1442000 c5 = -3.4 b1 = .159E-4 b5 = 461.6319 b6 = 2450000 b7 = -.15E-5 b8 = 3.6 end bix EoS = 8 | H= -959000.0 MnO(2)O2(.5) GH = -992899.7 S0 = 113.7 V0 = 3.137 c1 = 145.1 c2 = .23534E-1 c3 = 721600 c5 = -1008.4 b1 = .291E-4 b5 = 364.4962 b6 = 2230000 b7 = -.18E-5 b8 = 4.04 end NiO EoS = 8 | H= -239470.0 NiO(1) GH = -250799.7 S0 = 38 V0 = 1.097 c1 = 47.7 c2 = .7824E-2 c3 = -392500 b1 = .33E-4 b5 = 418.0818 b6 = 2000000 b7 = -.2E-5 b8 = 3.94 transition = 1 type = 4 t1 = 520 t2 = 5.7 end pnt EoS = 8 | H= -1361380 TiO2(1)MnO(1) GH = -1393133 S0 = 106.5 V0 = 3.288 c1 = 143.5 c2 = .3373E-2 c3 = -1940700 c5 = -407.6 b1 = .24E-4 b5 = 383.4174 b6 = 1700000 b7 = -.49E-5 b8 = 8.3 end geik EoS = 8 | H= -1568980 MgO(1)TiO2(1) GH = -1591222 S0 = 74.6 V0 = 3.086 c1 = 136.1 c2 = .1656E-2 c3 = -2533000 c5 = -283.9 b1 = .215E-4 b5 = 497.9401 b6 = 1700000 b7 = -.49E-5 b8 = 8.3 transition = 1 type = 5 t1 = 8310 t3 = 8300 t5 = 1 t6 = .5 end ilm EoS = 8 | H= -1232290 TiO2(1)FeO(1) GH = -1264341 S0 = 107.5 V0 = 3.169 c1 = 125.3 c2 = .9938E-2 c3 = -2458100 c5 = -25.9 b1 = .24E-4 b5 = 380.6729 b6 = 1700000 b7 = -.49E-5 b8 = 8.3 transition = 1 type = 5 t1 = 7060 t3 = 7050 t5 = 1 t6 = .5 end bdy EoS = 8 | H= -1100310 ZrO2(1) GH = -1115337 S0 = 50.4 V0 = 2.115 c1 = 89.6 c2 = .354E-3 c3 = -853100 c5 = -413.7 b1 = .2E-4 b5 = 457.6592 b6 = 953000 b7 = -.41E-5 b8 = 3.88 end bdyT EoS = 8 | H= -1096010 ZrO2(1) GH = -1111931 S0 = 53.4 V0 = 2.115 c1 = 89.6 c2 = .354E-3 c3 = -853100 c5 = -413.7 b1 = .2E-4 b5 = 438.7789 b6 = 953000 b7 = -.41E-5 b8 = 3.88 end bdyC EoS = 8 | H= -1085950 ZrO2(1) GH = -1103004 S0 = 57.2 V0 = 2.495 c1 = 89.6 c2 = .354E-3 c3 = -853100 c5 = -413.7 b1 = .2E-4 b5 = 416.989 b6 = 953000 b7 = -.41E-5 b8 = 3.88 end ten EoS = 8 | H= -156100.0 CuO(1) GH = -168801.2 S0 = 42.6 V0 = 1.222 c1 = 31 c2 = .1374E-1 c3 = -1258000 c5 = 369.3 b1 = .357E-4 b5 = 383.4174 b6 = 2000000 b7 = -.2E-5 b8 = 3.94 end cup EoS = 8 | H= -170600.0 O2(-.5)CuO(2) GH = -198149.1 S0 = 92.4 V0 = 2.344 c1 = 110.3 c5 = -674.8 b1 = .333E-4 b5 = 285.6069 b6 = 1310000 b7 = -.43E-5 b8 = 5.7 end sp EoS = 8 | H= -2300080 MgO(1)Al2O3(1) GH = -2324120 S0 = 80.63 V0 = 3.978 c1 = 200.5 c2 = .6252E-2 c3 = -2996400 c5 = -888.4 b1 = .193E-4 b5 = 592.252 b6 = 1922000 b7 = -.21E-5 b8 = 4.04 transition = 1 type = 5 t1 = 13930 t3 = -3600 t5 = 2 t6 = .6666667 end nsp EoS = 8 | H= -2300080 MgO(1)Al2O3(1) GH = -2324120 S0 = 80.63 V0 = 3.978 c1 = 200.5 c2 = .6252E-2 c3 = -2996400 c5 = -888.4 b1 = .193E-4 b5 = 592.252 b6 = 1922000 b7 = -.21E-5 b8 = 4.04 end herc EoS = 8 | H= -1949490 Al2O3(1)FeO(1) GH = -1983449 S0 = 113.9 V0 = 4.075 c1 = 184.9 c2 = .1417E-1 c3 = -3674800 c5 = -404 b1 = .206E-4 b5 = 468.3105 b6 = 1922000 b7 = -.21E-5 b8 = 4.04 transition = 1 type = 5 t1 = 13930 t3 = -3600 t5 = 2 t6 = .6666667 end nherc EoS = 8 | H= -1949490 Al2O3(1)FeO(1) GH = -1983449 S0 = 113.9 V0 = 4.075 c1 = 184.9 c2 = .1417E-1 c3 = -3674800 c5 = -404 b1 = .206E-4 b5 = 468.3105 b6 = 1922000 b7 = -.21E-5 b8 = 4.04 end mt EoS = 8 | H= -1114220 FeO(3)O2(.5) GH = -1158018 S0 = 146.9 V0 = 4.452 c1 = 262.5 c2 = -.7205E-2 c3 = -1926200 c5 = -1655.7 b1 = .371E-4 b5 = 387.8112 b6 = 1857000 b7 = -.22E-5 b8 = 4.05 transition = 1 type = 4 t1 = 848 t2 = 35 end mft EoS = 8 | H= -1442210 MgO(1)FeO(2)O2(.5) GH = -1478286 S0 = 121 V0 = 4.457 c1 = 270.5 c2 = -.7505E-2 c3 = -999200 c5 = -2022.4 b1 = .363E-4 b5 = 448.29 b6 = 1857000 b7 = -.22E-5 b8 = 4.05 transition = 1 type = 4 t1 = 665 t2 = 17 end qnd EoS = 8 | H= -2157830 MgO(2)TiO2(1) GH = -2191133 S0 = 111.7 V0 = 4.529 c1 = 161.7 c2 = .3286E-1 c3 = -2382200 c5 = -278.6 b1 = .263E-4 b5 = 474.882 b6 = 1470000 b7 = -.272E-5 b8 = 4 end usp EoS = 8 | H= -1495670 TiO2(1)FeO(2) GH = -1546654 S0 = 171 V0 = 4.682 c1 = 129.5 c2 = .48696E-1 c3 = -3739000 c5 = 690.2 b1 = .386E-4 b5 = 344.5576 b6 = 1470000 b7 = -.272E-5 b8 = 4 transition = 1 type = 5 t1 = 1000 t3 = 900 t5 = 1 t6 = .5 end picr EoS = 8 | H= -1764170 MgO(1)Cr2O3(1) GH = -1799441 S0 = 118.3 V0 = 4.356 c1 = 196.1 c2 = .5398E-2 c3 = -3126000 c5 = -616.9 b1 = .26E-4 b5 = 455.6984 b6 = 1922000 b7 = -.21E-5 b8 = 4.04 end br EoS = 8 | H= -925630.0 MgO(1)H2O(1) GH = -944473.1 S0 = 63.2 V0 = 2.463 c1 = 158.4 c2 = -.4076E-2 c3 = -1052300 c5 = -1171.3 b1 = .62E-4 b5 = 557.4423 b6 = 415000 b7 = -.155E-4 b8 = 6.45 end dsp EoS = 8 | H= -999740.0 Al2O3(.5)H2O(.5) GH = -1010026 S0 = 34.5 V0 = 1.786 c1 = 145.1 c2 = .8709E-2 c3 = 584400 c5 = -1741.1 b1 = .357E-4 b5 = 706.0073 b6 = 2280000 b7 = -.18E-5 b8 = 4.04 end gth EoS = 8 | H= -561680.0 FeO(1)O2(.25)H2O(.5) GH = -579658.4 S0 = 60.3 V0 = 2.082 c1 = 139.3 c2 = .147E-3 c3 = -212700 c5 = -1077.8 b1 = .435E-4 b5 = 494.3528 b6 = 2500000 b7 = -.16E-5 b8 = 4.03 end cc EoS = 8 | H= -1207740 CaO(1)CO2(1) GH = -1235319 S0 = 92.5 V0 = 3.689 c1 = 140.9 c2 = .5029E-2 c3 = -950700 c5 = -858.4 b1 = .252E-4 b5 = 426.4635 b6 = 733000 b7 = -.55E-5 b8 = 4.06 transition = 1 type = 4 t1 = 1240 t2 = 10 t3 = .4E-1 end arag EoS = 8 | H= -1207640 CaO(1)CO2(1) GH = -1234414 S0 = 89.8 V0 = 3.415 c1 = 167.1 c2 = .10695E-1 c3 = 162000 c5 = -1564.9 b1 = .614E-4 b5 = 435.9016 b6 = 614000 b7 = -.96E-5 b8 = 5.87 end mag EoS = 8 | H= -1110880 MgO(1)CO2(1) GH = -1130409 S0 = 65.5 V0 = 2.803 c1 = 186.4 c2 = -.3772E-2 c5 = -1886.2 b1 = .338E-4 b5 = 544.3193 b6 = 1028000 b7 = -.53E-5 b8 = 5.41 end sid EoS = 8 | H= -762140.0 FeO(1)CO2(1) GH = -789957.4 S0 = 93.3 V0 = 2.943 c1 = 168.4 c5 = -1483.6 b1 = .439E-4 b5 = 423.745 b6 = 1200000 b7 = -.34E-5 b8 = 4.07 end rhc EoS = 8 | H= -892280.0 MnO(1)CO2(1) GH = -921498.7 S0 = 98 V0 = 3.107 c1 = 169.5 c5 = -1534.3 b1 = .244E-4 b5 = 408.4485 b6 = 953000 b7 = -.41E-5 b8 = 3.88 end dol EoS = 8 | H= -2326200 MgO(1)CaO(1)CO2(2) GH = -2372741 S0 = 156.1 V0 = 6.429 c1 = 358.9 c2 = -.4905E-2 c5 = -3456.2 b1 = .328E-4 b5 = 482.3583 b6 = 943000 b7 = -.4E-5 b8 = 3.74 transition = 1 type = 5 t1 = 11910 t2 = .16E-1 t3 = 11900 t4 = .16E-1 t5 = 1 t6 = 1 end ank EoS = 8 | H= -1971310 CaO(1)FeO(1)CO2(2) GH = -2027499 S0 = 188.46 V0 = 6.606 c1 = 341 c2 = -.1161E-2 c5 = -3054.8 b1 = .346E-4 b5 = 420.628 b6 = 914000 b7 = -.43E-5 b8 = 3.88 transition = 1 type = 5 t1 = 11910 t2 = .16E-1 t3 = 11900 t4 = .16E-1 t5 = 1 t6 = 1 end syv EoS = 8 | H= -436500.0 K2O(.5)Cl2(.5)O2(-.25) GH = -461127.2 S0 = 82.6 V0 = 3.752 c1 = 46.2 c2 = .1797E-1 b1 = .1109E-3 b5 = 222.7901 b6 = 170000 b7 = -.294E-4 b8 = 5 end hlt EoS = 8 | H= -411300.0 Na2O(.5)Cl2(.5)O2(-.25) GH = -432796.6 S0 = 72.1 V0 = 2.702 c1 = 45.2 c2 = .1797E-1 b1 = .1147E-3 b5 = 250.3177 b6 = 238000 b7 = -.21E-4 b8 = 5 end pyr EoS = 8 | H= -171640.0 FeO(1)O2(-.5)S2(1) GH = -187412.1 S0 = 52.9 V0 = 2.394 c1 = 37.3 c2 = .26715E-1 c3 = -1817000 c5 = 649.3 b1 = .31E-4 b5 = 441.8167 b6 = 1395000 b7 = -.29E-5 b8 = 4.09 end trot EoS = 8 | H= -99030.00 FeO(1)O2(-.5)S2(.5) GH = -118558.8 S0 = 65.5 V0 = 1.819 c1 = 50.2 c2 = .11052E-1 c3 = -940000 b1 = .568E-4 b5 = 271.3958 b6 = 658000 b7 = -.63E-5 b8 = 4.17 transition = 1 type = 4 t1 = 598 t2 = 12 t3 = .41E-1 end tro EoS = 8 | H= -97770.00 FeO(1)O2(-.5)S2(.5) GH = -118879 S0 = 70.8 V0 = 1.819 c1 = 50.2 c2 = .11052E-1 c3 = -940000 b1 = .573E-4 b5 = 254.2065 b6 = 658000 b7 = -.63E-5 b8 = 4.17 transition = 1 type = 4 t1 = 598 t2 = 12 t3 = .41E-1 end lot EoS = 8 | H= -102170.0 FeO(1)O2(-.5)S2(.5) GH = -120059 S0 = 60 V0 = 1.818 c1 = 50.2 c2 = .11052E-1 c3 = -940000 b1 = .493E-4 b5 = 291.8771 b6 = 658000 b7 = -.63E-5 b8 = 4.17 transition = 1 type = 4 t1 = 420 t2 = 10 end trov EoS = 8 | H= -96020.00 FeO(.88)O2(-.44)S2(.5) GH = -113163.6 S0 = 57.5 V0 = 1.738 c1 = 51.1 c2 = .8307E-2 c3 = -669700 b1 = .594E-4 b5 = 286.6331 b6 = 658000 b7 = -.63E-5 b8 = 4.17 transition = 1 type = 4 t1 = 595 t2 = 10 t3 = .16E-1 end any EoS = 8 | H= -1434400 CaO(1)O2(1.5)S2(.5) GH = -1466272 S0 = 106.9 V0 = 4.594 c1 = 128.7 c2 = .48545E-1 c3 = -1223000 c5 = -560.5 b1 = .418E-4 b5 = 438.4774 b6 = 543800 b7 = -.77E-5 b8 = 4.19 end iron EoS = 8 | H= 0.000000 FeO(1)O2(-.5) GH = -8076.883 S0 = 27.09 V0 = .709 c1 = 46.2 c2 = .5159E-2 c3 = 723100 c5 = -556.2 b1 = .356E-4 b5 = 317.2085 b6 = 1640000 b7 = -.31E-5 b8 = 5.16 transition = 1 type = 4 t1 = 1042 t2 = 8.3 end Ni EoS = 8 | H= 0.000000 NiO(1)O2(-.5) GH = -8905.74 S0 = 29.87 V0 = .659 c1 = 49.8 c3 = 585900 c5 = -533.9 b1 = .428E-4 b5 = 292.9221 b6 = 1905000 b7 = -.22E-5 b8 = 4.25 transition = 1 type = 4 t1 = 631 t2 = 3 end Cu EoS = 8 | H= 0.000000 O2(-.5)CuO(1) GH = -9880.691 S0 = 33.14 V0 = .711 c1 = 12.4 c2 = .922E-2 c3 = -379900 c5 = 233.5 b1 = .358E-4 b5 = 268.7216 b6 = 1625000 b7 = -.26E-5 b8 = 4.24 end gph EoS = 8 | H= 0.000000 O2(-1)CO2(1) GH = -1717.344 S0 = 5.76 V0 = .53 c1 = 34.3 c3 = -240700 c5 = -403.8 b1 = .165E-4 b5 = 871.8033 b6 = 312000 b7 = -.125E-4 b8 = 3.9 end diam EoS = 8 | H= 1890.000 O2(-1)CO2(1) GH = 1186.366 S0 = 2.36 V0 = .342 c1 = 40 c3 = -28500 c5 = -580.5 b1 = .4E-5 b5 = 1208.636 b6 = 4465000 b7 = -.36E-6 b8 = 1.61 end S EoS = 8 | H= 0.000000 S2(.5) GH = -9555.707 S0 = 32.05 V0 = 1.551 c1 = 56.6 c2 = -.4557E-2 c3 = 638000 c5 = -681.8 b1 = .64E-4 b5 = 276.3315 b6 = 145000 b7 = -.48E-4 b8 = 7 end H2O EoS = 101 | H= -241810.0 H2O(1) GH = -298100.7 S0 = 188.8 c1 = 40.1 c2 = .8656E-2 c3 = 487500 c5 = -251.2 end CO2 EoS = 102 | H= -393510.0 CO2(1) GH = -457224.7 S0 = 213.7 c1 = 87.8 c2 = -.2644E-2 c3 = 706400 c5 = -998.9 end CO EoS = 103 | H= -110530.0 O2(-.5)CO2(1) GH = -169465.3 S0 = 197.67 c1 = 45.7 c2 = -.97E-4 c3 = 662700 c5 = -414.7 end CH4 EoS = 104 | H= -74810.00 O2(-2)H2O(2)CO2(1) GH = -130343.4 S0 = 186.26 c1 = 150.1 c2 = .2063E-2 c3 = 3427700 c5 = -2650.4 end C2H6 EoS = 116 | HSC/MRK Ethane H2O(3)CO2(2)O2(-3.5) GH = -152.135425062466d3 S0 = 229.600929272063 c1 = -6.566 c2 = 175.454d-3 c3 = 5.878d5 c4 = -64.885d-6 transition = 1 type = 2 t1 = 1400 t4 = 39.896 t5 = 92.427d-3 t6 = -38.222d5 t7 = -22.727d-6 transition = 2 type = 2 t1 = 3400 t4 = 127.129 t5 = 12.005d-3 t6 = -354.785d5 t7 = -1.550d-6 end O2 EoS = 107 | H= 0.000000 O2(1) GH = -61180.38 S0 = 205.2 c1 = 48.3 c2 = -.691E-3 c3 = 499200 c5 = -420.7 end H2 EoS = 105 | H= 0.000000 O2(-.5)H2O(1) GH = -38968.2 S0 = 130.7 c1 = 23.3 c2 = .4627E-2 c5 = 76.3 end S2 EoS = 1 | H= 128540.0 S2(1) GH = 59667.35 S0 = 231 c1 = 37.1 c2 = .2398E-2 c3 = -161000 c5 = -65 end H2S EoS = 106 | H= -20300.00 O2(-.5)H2O(1)S2(.5) GH = -81650.32 S0 = 205.77 c1 = 47.4 c2 = .1024E-1 c3 = 615900 c5 = -397.8 end syvL EoS = 9 | H= -417410.0 K2O(.5)Cl2(.5)O2(-.25) GH = -445585.2 S0 = 94.5 V0 = 3.822 c1 = 66.9 b1 = .301E-3 b5 = -20 b6 = 56000 b7 = -.83E-4 b8 = 4.65 end hltL EoS = 9 | H= -392990.0 Na2O(.5)Cl2(.5)O2(-.25) GH = -416871.8 S0 = 80.1 V0 = 2.938 c1 = 72 c2 = -.3223E-2 b1 = .295E-3 b5 = -15 b6 = 64000 b7 = -.72E-4 b8 = 4.61 end perL EoS = 9 | H= -654200.0 MgO(1) GH = -635029 S0 = -64.3 V0 = .839 c1 = 99 b1 = .226E-3 b5 = -41 b6 = 362000 b7 = -.278E-4 b8 = 10.06 end limL EoS = 9 | H= -692330.0 CaO(1) GH = -678167.9 S0 = -47.5 V0 = 1.303 c1 = 99 b1 = .175E-3 b5 = -41 b6 = 362000 b7 = -.278E-4 b8 = 10.06 end corL EoS = 9 | H= -1632150 Al2O3(1) GH = -1636592 S0 = 14.9 V0 = 3.369 c1 = 157.6 b1 = .703E-4 b5 = -35 b6 = 150000 b7 = .4E-4 b8 = 6 end eskL EoS = 9 | H= -1062190 Cr2O3(1) GH = -1081063 S0 = 63.3 V0 = 3.709 c1 = 157.6 b1 = .703E-4 b5 = -35 b6 = 150000 b7 = .4E-4 b8 = 6 end hemL EoS = 9 | H= -875140.0 FeO(2)O2(.5) GH = -865241.4 S0 = -33.2 V0 = 3.2208 c1 = 229 b1 = .1953E-3 b5 = -46 b6 = 230000 b7 = -.174E-4 b8 = 4 end qL EoS = 9 | H= -921010.0 SiO2(1) GH = -925899.7 S0 = 16.4 V0 = 2.73 c1 = 82.5 b5 = -35 b6 = 220000 b7 = -.43E-4 b8 = 9.46 end h2oL EoS = 9 | H= -281640.0 H2O(1) GH = -301496.8 S0 = 66.6 V0 = 1.3355 c1 = 65 b1 = .626E-3 b5 = -10.6 b6 = 42280 b7 = -.946E-4 b8 = 4 end foL EoS = 9 | H= -2237200 MgO(2)SiO2(1) GH = -2218715 S0 = -62 V0 = 4.312 c1 = 269.4 b1 = .92E-4 b5 = -44 b6 = 362000 b7 = -.278E-4 b8 = 10.06 end faL EoS = 9 | H= -1462820 SiO2(1)FeO(2) GH = -1491442 S0 = 96 V0 = 4.677 c1 = 243.7 b1 = .1071E-3 b5 = -55 b6 = 290000 b7 = -.359E-4 b8 = 10.42 end woL EoS = 9 | H= -1642550 SiO2(1)CaO(1) GH = -1649258 S0 = 22.5 V0 = 3.985 c1 = 167.4 b1 = .669E-4 b5 = -20 b6 = 325000 b7 = -.308E-4 b8 = 9.38 end enL EoS = 9 | H= -3096280 MgO(2)SiO2(2) GH = -3095087 S0 = -4 V0 = 6.984 c1 = 353.6 b1 = .681E-4 b5 = -24 b6 = 218000 b7 = -.33E-4 b8 = 7.2 end diL EoS = 9 | H= -3193770 MgO(1)SiO2(2)CaO(1) GH = -3206322 S0 = 42.1 V0 = 7.288 c1 = 334 b1 = .851E-4 b5 = -37.3 b6 = 249000 b7 = -.323E-4 b8 = 8.04 end silL EoS = 9 | H= -2593500 Al2O3(1)SiO2(1) GH = -2596481 S0 = 10 V0 = 6.051 c1 = 253 b1 = .408E-4 b5 = -29 b6 = 220000 b7 = -.289E-4 b8 = 6.36 end anL EoS = 9 | H= -4277950 Al2O3(1)SiO2(2)CaO(1) GH = -4286596 S0 = 29 V0 = 10.014 c1 = 430 b1 = .514E-4 b5 = -55 b6 = 210000 b7 = -.304E-4 b8 = 6.38 end kspL EoS = 9 | H= -3985380 Al2O3(.5)SiO2(3)K2O(.5) GH = -4023901 S0 = 129.2 V0 = 11.431 c1 = 368 b1 = .493E-4 b5 = -9 b6 = 173000 b7 = -.393E-4 b8 = 6.84 end abL EoS = 9 | H= -3925420 Na2O(.5)Al2O3(.5)SiO2(3) GH = -3970113 S0 = 149.9 V0 = 10.858 c1 = 358 b1 = .337E-4 b5 = -26 b6 = 176000 b7 = -.815E-4 b8 = 14.35 end neL EoS = 9 | H= -2117030 Na2O(.5)Al2O3(.5)SiO2(1) GH = -2132802 S0 = 52.9 V0 = 5.2 c1 = 216.5 b1 = .137E-3 b5 = -8 b6 = 250000 b7 = -.295E-4 b8 = 7.37 end lcL EoS = 9 | H= -3068530 Al2O3(.5)SiO2(2)K2O(.5) GH = -3098941 S0 = 102 V0 = 8.59 c1 = 287 b1 = .67E-4 b5 = 639.1827 b6 = 175000 b7 = -.394E-4 b8 = 7 end ruL EoS = 9 | H= -948480.0 TiO2(1) GH = -948778.1 S0 = 1 V0 = 1.7032 c1 = 111.8 b1 = .2901E-3 b5 = -35 b6 = 149000 b7 = -.34E-4 b8 = 8 end bdyL EoS = 9 | H= -1031870 ZrO2(1) GH = -1046450 S0 = 48.9 V0 = 1.83 c1 = 90 b1 = .2E-3 b5 = -30 b6 = 149000 b7 = -.34E-4 b8 = 8 end |======================================================================================= | data from external sources: |======================================================================================= ilm_nol EoS = 8 | H= -1230460. Ilmenite with landau transition suppressed for Ilm(WPH) model. TiO2(1)FeO(1) GH = -1264371 S0 = 107.5 V0 = 3.169 c1 = 138.9 c2 = .5081E-2 c3 = -1288800 c5 = -463.7 b1 = .24E-4 b5 = 380.6729 b6 = 1700000 b7 = -.49E-5 b8 = 8.3 end SO2 EoS = 108 | SO2,g SUPCRT DATA SULFUR-DIOXIDE ref:6,8 O2(1)S2(.5) G0 = -300194. S0 = 248.237 c1 = 46.1914 c2 = .786592E-2 c3 = -769856 end N2 EoS = 110 | HSC to 1500 K N2(1) G0 = 0 S0 = 191.610 c1 = 27.75318 c2 = 0.60476d-3 c3 = 0.72831d5 c4 = 4.95984d-6 transition = 1 type = 2 t1 = 700 t4 = 23.52868 t5 = 12.11645d-3 t6 = 1.21039d5 t7 = -3.0762d-6 end Cv EoS = 1 | COVELLITE CuS ref:1 O2(-.5)S2(.5)CuO(1) G0 = -52768.6 S0 = 66.5256 V0 = 2.042 c1 = 44.3504 c2 = .110458E-1 end Bn EoS = 1 | BORNITE Cu5FeS4 ref:1,16 FeO(1)O2(-3)S2(2)CuO(5) G0 = -362770. S0 = 415.429 V0 = 9.86 c1 = 208.196 c2 = .146775 c3 = -564840 transition = 1 type = 2 t1 = 485 t3 = 12.3363 t4 = -143.553 t5 = 1.03345 end Cc EoS = 1 | CHALCOCITE Cu2S ref:1 O2(-1)S2(.5)CuO(2) G0 = -86299.2 S0 = 120.918 V0 = 2.748 c1 = 52.8439 c2 = .787429E-1 transition = 1 type = 2 t1 = 376 t3 = 10.2375 t4 = 112.047 t5 = -.307524E-1 end Ccp EoS = 1 | CHALCOPYRITE CuFeS2 ref:1,16 FeO(1)O2(-1)S2(1)CuO(1) G0 = -187862. S0 = 130.332 V0 = 4.283 c1 = 86.9854 c2 = .535552E-1 c3 = -560656 transition = 1 type = 2 t1 = 830 t3 = 12.1235 t4 = -591.618 t5 = .87864 end Azr EoS = 1 | AZURITE Cu3(OH)2(CO3)2 ref:1 H2O(1)CO2(2)CuO(3) G0 = -1399201 S0 = 280.202 V0 = 9.101 c1 = 154.306 c2 = .324009 c3 = -384928 end Mal EoS = 1 | MALACHITE Cu2(OH)2(CO3) ref:1 H2O(1)CO2(1)CuO(2) G0 = -896230. S0 = 186.188 V0 = 5.486 c1 = 116.148 c2 = .183175 c3 = -560656 end NH3 EoS = 111 | HSC N2(0.5)O2(-.75)H2O(1.5) GH = -103.416906d3 S0 = 192.777591247135 c1 = 24.90389 c2 = 36.32064d-3 c3 = 0.48713d5 c4 = -4.60882d-6 transition = 1 type = 2 t1 = 1000 t4 = 65.06398 t5 = 7.64413d-3 t6 = -165.83662d5 t7 = -0.85095d-6 end fran EoS = 8 | HSC data for Ni olivine, volume = fa - 0.2 J/bar SiO2(1)NiO(2) GH = -1436.24550636556d3 S0 = 110.038861980792 V0 = 4.431 c1 = 163.17462 c2 = 19.7524293937683d-3 c3 = -24.3089659423828d5 c4 = 8.82611d-6 b1 = .282E-4 b5 = 379.7022 b6 = 1256000 b7 = -.37E-5 b8 = 4.68 end mil EoS = 8 | HSC caloric data (to 1250 K, mp) + vol from www.webmineral.com/data/Millerite.shtml NiO(1)O2(-.5)S2(.5) G0 = -109.805191692176d3 S0 = 53.0112172929809 V0 = 1.690 c1 = 45.99998 c2 = 17.10001d-3 c3 = -3.51d5 b1 = .573E-4 b5 = 254.2065 b6 = 658000 b7 = -.63E-5 b8 = 4.17 transition = 1 type = 2 t1 = 652 t3 = 9.883 t4 = 34.60001 t5 = 28.49999d-3 end